Master's Dissertation
DOI
https://doi.org/10.11606/D.97.2012.tde-01102013-143822
Document
Author
Full name
Luiz Alberto dos Santos
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Lorena, 2012
Supervisor
Committee
Nunes, Carlos Angelo (President)
Candioto, Katia Cristiane Gandolpho
Santos, Claudinei dos
Title in Portuguese
Processamento e caracterização da liga 66%Co-28%Cr-6%Mo para implantes
Keywords in Portuguese
Caracterização mecânica
Caracterização Microestrutural
Forjamento a quente
Implantes
Liga 66Co-28Cr-6Mo
Abstract in Portuguese
Neste trabalho foram avaliadas as condições de processamento e caracterização da liga 66Co-28Cr-6Mo utilizada em implantes. Cada lingote foi produzido por meio de fusão a arco voltáico, sob atmosfera de argônio em um cadinho de cobre refrigerado à água. Os resultados foram comparados com aqueles de uma barra da liga 66Co-28Cr-6Mo comercial. A temperatura de forjamento a quente da liga é em torno de 1200º C, pois temperaturas menores levam a fraturas do material no decorrer do forjamento. Na análise química realizada na liga 66Co-28Cr-6Mo obteve-se uma concentração de 0,038%C, ou seja, esta concentração encontrada nos lingotes da liga 66Co-28Cr-6Mo produzida estão dentro das especificações da norma ASTM F1537 para a liga com baixo teor de carbono (0,14%C). Os lingotes apresentaram uma microestrutura policristalina, com presença de defeitos volumétricos (poros) possívelmente advindos do processo de solidificação. Foram realizados ensaios de oxidação nas temperaturas de 1200 oC, 1100 oC, 1000 oC e 900 oC por cerca de 30 minutos para avaliar o grau de oxidação da liga de 66Co-28Cr-6Mo em elevadas temperaturas, pois a conformação mecânica da liga é realizada a quente conforme descrito na norma ASTM F1537. O limite de escoamento à tração da liga 66Co-28Cr-6Mo na condição bruta é em média de 750 MPa e o módulo de elasticidade da mesma liga é, aproximadamente de 158 GPa. Notou-se na liga 66Co-28Cr-6Mo comercial uma microestrutura com grãos refinados, proveniente do processo de forjamento a quente. Além disso, observa-se a presença de maclas, porém não se pode afirmar se este defeito é devido à deformação plástica ou tratamento térmico. O limite de escoamento à tração da liga 66Co-28Cr-6Mo comercial foi de 975 MPa e módulo de elasticidade é, de aproximadamente de 203 GPa. A densidade de corrente de corrosão das ligas 66Co-28Cr-6Mo produzida e comercial são respectivamente 1,9x10-7 e 1,5x10-7 Acm-2. Estes valores indicam uma alta resistência à corrosão de ambas as ligas em solução de Ringer. As amostras das ligas 66Co-28Cr-6Mo comercial e produzida apresentaram uma curva de viabilidade celular acima da linha do índice de citotoxicidade (IC50%) = 50%, ou seja, as ligas são consideradas não tóxica.
Title in English
Processing and Characterization of the 66Co-28Cr-6Mo (%weight) alloy for implants
Keywords in English
Alloy 28Cr-66Co-6Mo
Hot forging
Implants
Mechanical characterization
Microstructure characterization
Abstract in English
In this study we evaluated the processing conditions and characterization alloy 28%Cr 66%Co-6%Mo used in implants. Each ingot was produced by through arc melting arcing under argon atmosphere in a water-cooled copper crucible. The results were compared with those of a commercial bar 66Co-28Cr-6Mo alloy. The temperature of hot forging 66Co-28Cr-6Mo alloy should be around 1200 º C because lower temperatures lead to fracture of the material during forging. In the chemical analysis performed on the alloy 66Co-28Cr-6Mo obtained a concentration 0,038 %C. Indeed the alloy 66Co-28Cr-6Mo produced are within the specifications of ASTM F1537 for the alloy with low carbon (0.14% C). The ingots had a polycrystalline microstructure with the presence of volumetric defects (pores) possibly arised from the solidification process. Oxidation tests were carried out at temperatures of 1200 oC, 1100 oC 1000 oC and 900 oC for about 30 minutes to evaluate the degree of oxidation of 66Co-28Cr -6Mo alloy at high temperatures because of the mechanical forming league will be held hot. The tensile yield strength of the 66Co-28Cre-6Mo alloy is provided and gross average of 750 MPa and elasticity of the same alloy is approximately 158 GPa. It was noted in the 66Co-28Cr-6Mo alloy commercial grain microstructure with a refined, from the hot forging process. Moreover, observed the presence of twinned, but one cannot say whether this defect is due to plastic deformation or heat treatment. The tensile yield strength of the 66%Co-28%Cr-6%Mo alloy trade was 975 MPa and modulus of elasticity is of approximately 203 GPa. The corrosion current density of the 66Co-28Cr-6Mo alloys and commercial produced are respectively 1,9.10-7 and 1,5.10-7 Acm-2. These values indicate a high corrosion resistence of both alloys in Ringer's solution. Samples of the commercial and produced 66Co-28Cr-6Mo alloys a curve above the cell viability index of citotoxicity (IC50%) = 50% the alloys are considered non-toxic.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
EMD12003_C.pdf (2.26 Mbytes)
Publishing Date
2013-10-01
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.