Tese de Doutorado
DOI
10.11606/T.88.2000.tde-26102005-142234
Documento
Autor
Nome completo
Sergio Mazzer Rossitti
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2000
Orientador
Banca examinadora
Rollo, Joao Manuel Domingos de Almeida (Presidente)
Balancin, Oscar
Button, Sergio Tonini
Crnkovic, Ovidio Richard
Jorge Junior, Alberto Moreira
Título em português
Efeito do Nióbio na Microestrutura e nas Propriedades Mecânicas do Aço Inoxidável Superduplex Fundido SEW 410 W.Nr. 1.4517
Palavras-chave em português
aço inoxidável superduplex
efeito do Nb
microestrutura e propriedades mecânicas
Resumo em português
A produção economicamente viável dos aços inoxidáveis duplex, pressupõe a utilização de sucatas e retornos de ligas contendo altos teores de elementos como Cr, Ni e Mo. O aproveitamento destes materiais pode entretanto, introduzir na composição química outros elementos não previstos pela norma do material sendo produzido. Este trabalho estudou a influência do Nb na microestrutura e nas propriedades mecânicas do aço inoxidável superduplex fundido SEW 410 W. Nr. 1.4517, bem como sobre as etapas de fabricação de um produto fundido. Os teores de Nb estudados foram 0%, 0,2%, 0,5% e 1,5% (% em peso). Foi dado ênfase às microestruturas e propriedades no estado bruto de fundição, após tratamento térmico de solubilização e finalmente, após envelhecimento das amostras solubilizadas. Foram utilizadas diversas técnicas de avaliação microestrutural: microscopia ótica, metalografia quantitativa, microscopia eletrônica de varredura e de transmissão, análise química de microregiões com microssonda eletrônica, ensaios magnéticos via ferritoscópio e ensaios dilatométricos. Os ensaios mecânicos realizados foram: dureza, ensaio de tração e ensaio Charpy. A análise dos resultados demonstrou que o Nb causou uma sensível alteração na microestrutura e nas propriedades mecânicas da liga, dificultando o processo de produção de uma peça fundida.
Título em inglês
Effect of niobium on the microstructure and mechanical properties of cast super duplex stainless steel SEW 410 W. Nr.1.4517
Palavras-chave em inglês
effect of Nb
microstructure and mechanical properties
super duplex stainless steel
Resumo em inglês
To produce duplex stainless steel in an economic way it is necessary to use scrap and process returns containing high Cr, Ni and Mo contents. This procedure can result in an unexpected alloy chemical composition with some elements not included in the material standard. This work studied the Nb influence on the microstructure and mechanical properties of cast super duplex stainless steel SEW 410 W. Nr. 1.4517, as well as the influence over the fabrication process of a casting. The Nb contents studied were 0%, 0,2%, 0,5% and 1,5% (weight %). Emphasis was given to the microstructures and mechanical properties in as cast condition, after solution heat treatment and finally after aging of previous solution heat treated samples. Several microstructural analysis techniques were used: optical microscopy, quantitative metallography, scanning electron microscopy, transmission electron microscopy, chemical microanalysis using energy dispersive spectrometry, magnetic phase detection using feritscope and dilatometry. The mechanical testing realized were hardness testing, tension testing and Charpy impact testing. Results analysis demonstrated that Nb caused an appreciable change on microstructure and mechanical properties of the material, making difficult the fabrication process of a casting.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
tesesergiorossiti.pdf (197.08 Kbytes)
tesesergiorossiti2.pdf (14.12 Mbytes)
Data de Publicação
2005-11-09
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.