Dissertação de Mestrado
Documento
Autor
Nome completo
Lucas Ponez da Mota
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2010
Orientador
Banca examinadora
Maule, Agnieszka Joanna Pawlicka (Presidente)
Gonzalez, Jose Pedro Donoso
Pulcinelli, Sandra Helena
Título em português
Preparação e caracterização de eletrólitos sólidos poliméricos à base de gelatina comercial para aplicação em células solares.
Palavras-chave em português
Célula Solar
Condutividade
Eletrólitos
Gelatina
Resumo em português
O presente trabalho visou estudar e caracterizar eletrólitos sólidos poliméricos (ESP) à base de gelatina plastificada com glicerol, entrecruzada com formaldeído e contendo LiI/I2 para a aplicação em células solares. O objetivo foi obter os eletrólitos à base de gelatina comercial (Dr. Oetker) de origem animal, uma vez que a mistura de aminoácidos presentes na mesma apresenta propriedades mecânicas interessantes e torna-se um gel transparente na região do visível. Glicerol foi usado para promover a plastificação e o formaldeído para promover as ligações cruzadas na mistura das proteínas aumentando a estabilidade e resistência dos filmes. As fontes iônicas foram o LiI.2H2O e I2 na proporção de 10:1 m/m. O estudo revelou que as amostras apresentaram os valores de condutividade iônica de 7,68 x 10-5 S.cm-1, 6,38 x 10-5 S.cm-1, 8,81 x 10-5 S.cm-1, 9,97 x 10-5 S.cm-1 e 7,87 x 10-5 S.cm-1 dependendo da concentração da mistura LiI.2H2O / I2 . As medidas de condutividade em função da temperatura mostraram que o mecanismo que governa a condutividade é do tipo VTF. As análises de estrutura das membranas por difração de Raios-X mostraram o caráter predominantemente amorfo e as análises térmicas (DSC) os valores da temperatura de transição vítrea (Tg) da ordem de -77ºC. A transparência das amostras de 80 a 90% foi confirmada por espectroscopia UV-Vis e as análises microscópicas (MEV) mostraram a presença de pequenos pontos brancos nas superfícies das amostras. Os eletrólitos aplicados em um pequeno protótipo de célula solar renderam um máximo de 0,15% de eficiência.
Título em inglês
Preparation and characterization solid polymer electrolytes based of commercial gelatin for application in solar cells.
Palavras-chave em inglês
Gel electrolytess
Gelatin
Ionic condutivity
Solar Cell
Resumo em inglês
This present work aimed study and characterization of solid polymer electrolytes (SPE) based on gelatin plasticized with glycerol, crosslinked with formaldehyde and containing LiI/I2 for application in solar cells. The plan was to get the electrolytes based on commercial gelatin (Dr. Oetker) of animal, since the mixture of amino acids present interesting mechanical properties and becomes a transparent gel in the visible region. Glycerol was used to promote plasticization and formaldehyde to promote cross-linking of the mixture of proteins leading to increase the stability and strength of the films. The ion sources were LiI.2H2O and I2 at a ratio of 10:1 m/m. The study revealed that the samples showed the values of ionic conductivity of 7.68 x 10-5 S.cm-1, 6.38 x 10-5 S.cm-1, 8.81 x 10-5 S.cm-1, 9.97 x 10-5 S.cm-1 and 7.87 x 10-5 S.cm-1, depending on the concentration of the mixture LiI.2H2O / I2. Ionic conductivity measurements as a function of temperature revealed VTF conducting model. X-ray diffractogramms showed the predominantly amorphous nature and thermal analysis (DSC) values of the glass transition temperature (Tg) of about -77 ° C. The transparency of the samples of 80 and 90% was confirmed by UV-Vis and the microscopic analysis (SEM) showed the presence of small white points in the surface of the samples. The electrolytes used in small solar cell prototypes yielded a maximum of 0.15% efficiency.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2010-03-26
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2014. Todos os direitos reservados.