Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.88.2010.tde-23032010-170752
Document
Auteur
Nom complet
Yurika Okamoto Iwaki
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2010
Directeur
Jury
Maule, Agnieszka Joanna Pawlicka (Président)
Biaggio, Sonia Regina
Goncalves, Debora
Titre en portugais
Eletrólitos sólidos poliméricos a base de alginato de sódio
Mots-clés en portugais
Alginato de sódio
Condutividade iônica
Eletrólitos sólidos poliméricos
Polímeros naturais
Resumé en portugais
Este trabalho teve como objetivo principal a preparação e caracterização de filmes de alginato de sódio plastificado com glicerol. Foram preparadas amostras de filmes variando-se a concentração de ácido acético ou de perclorato de lítio, com a finalidade de otimizá-los como eletrólitos sólidos poliméricos (ESP) em dispositivos eletroquímicos, como sensores e baterias. Após o preparo dos filmes, estes foram caracterizados por análise elementar (AE), microscopia eletrônica de varredura (MEV), difração de raios-X, termogravimetria (TG), análise térmica mecânico dinâmica (DMTA), espectroscopia no UV-VIS, espectroscopia de infravermelho (IR) e espectroscopia de impedância eletroquímica (EIE). Os filmes preparados com alginato de sódio foram plastificados com 0,6 g de glicerol e apresentaram transparência nos comprimentos de onda da luz visível, boa condutividade iônica e maleabilidade. Através dos difratogramas de raios-X pode-se observar que os filmes possuem predominantemente caráter amorfo. O filme de alginato de sódio dopado com 0,3 mL ácido acético apresentou a melhor condutividade (8,7x10-5 S cm-1 a temperatura ambiente e de 1,15x10-3 S cm-1 a 80°C). Para amostras com quantidades maiores de ácido acético os filmes tornaram-se quebradiços e opacos. Para as amostras preparadas com perclorato de lítio a melhor condutividade obtida foi com o filme preparado utilizando 15% em massa de perclorato de lítio: 3,1x10-4 S cm-1 a temperatura ambiente e 1,2x10-3 S cm-1, a 80°C. As análises dos valores de condutividade em função da temperatura das amostras de alginato de sódio revelaram que este segue o modelo Vogel-Tamman-Fulcher (VTF) de condução, onde a movimentação das cadeias poliméricas auxilia na condução iônica. O valor de energia de ativação foi de 36,14 kJ mol-1 para a amostra com 0,3 mL de ácido acético foi de 36 kJ mol-1 para a amostra com 0,4 mL de ácido. Para os filmes preparados com 15% em massa de perclorato de lítio foi de 18,43 kJ mol-1. Essas novas membranas demonstraram ser candidata promissora para aplicação em diversos dispositivos eletroquímicos.
Titre en anglais
Solid polymer electrolytes based in sodium alginate.
Mots-clés en anglais
Ionic conductivity
Natural polymers
Sodium alginate
Solid polymer electrolytes
Resumé en anglais
The aim of this study was the preparation and characterization of sodium alginate membranes plasticized with glycerol. The samples were obtained with different concentration of acetic acid or lithium perchlorate in order to use them as solid polymer electrolytes (SPE) in electrochemical devices, such as sensors and batteries. The films were characterized by elemental analysis (EA), scanning electron microscopy (SEM), X-ray, thermogravimetry (TG), dynamic-mechanical thermal analysis (DMTA), UV-visible spectroscopy, infrared spectroscopy (IR) and electrochemical impedance spectroscopy (IES). The samples plasticized with 0.6 g of glycerol showed good transparency, good ionic conductivity and flexibility. X-ray diffractograms evidenced predominantly amorphous state of the samples. The best ionic conductivity results of 8.7 x 10 -5 S cm -1 at room temperature and 1.15 x 10 - 3 S cm -1 at 80 ° C were obtained with sodium alginate samples containing 0.3 mL of acetic acid. Samples with larger amounts of acid became brittle and opaque. The best conductivity values of 3.1 x10 -4 S cm -1 at room temperature and 1, 2 x10 -3 S cm -1 at 80 ° C were obtained for the samples containing 15 wt.% of lithium perchlorate.. The analysis of the conductivity as a function of temperature revealed that they follow the Vogel-Tamman-Fulcher (VTF) conductivity model. The activation energy were 36, 14 kJ mol -1 for the sample with 0.3 mL of acetic acid and 36 kJ mol -1 for the sample with 0.4 mL of acid. The sample with 15 wt.% of lithium perchlorate showed activation energy of 18.43 kJ mol -1. This new ionic conducting membranes are good candidates to be used as electrolytes in electrochemical devices.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
YurikaMedefendida.pdf (2.04 Mbytes)
YurikaMErevisada.pdf (2.42 Mbytes)
Date de Publication
2010-03-25
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.