Tesis Doctoral
DOI
https://doi.org/10.11606/T.88.2016.tde-16092016-160549
Documento
Autor
Nombre completo
Adnauêr Tarquinio Daltro
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2000
Director
Tribunal
Gomes, Samuel Irati Novaes (Presidente)
Bolfarini, Claudemiro
Calil Júnior, Carlito
Ferraresi, Valtair Antonio
Malite, Maximiliano
Título en portugués
Soldagem a arco elétrico com proteção gasosa em juntas de chapas finas de aço
Palabras clave en portugués
Aço zincado
Chapa fina
Distorções
Soldagem
Resumen en portugués
O uso de chapas finas de aço, revestidas ou não, tem sido crescente nos últimos anos, principalmente aquelas que tem revestimento à base de zinco. Isto ocorre tanto na indústria automobilística e mecânica como na construção civil, que geralmente fabricam suas peças e estruturas utilizando um procedimento de soldagem. O objetivo deste trabalho é estabelecer procedimentos de soldagem à arco elétrico com proteção gasosa - GMAW - com transferência por curto circuito, para elementos de chapa fina de aço carbono não revestido e aço zincado, de modo a se obter junções de qualidade aceitável e diminuição das distorções decorrentes dos ciclos térmicos presentes durante a soldagem e, consequentemente a redução das tensões residuais. Em termos de qualidade da solda, propões-se uma combinação de consumíveis disponíveis no mercado, de modo a reduzir os defeitos como: porosidade, respingos, trincas e perda de revestimento. No caso das chapas finas de aço zincado, a melhor combinação de consumíveis encontrada foi: arame com baixo teor de desoxidantes, ER70S-3, e como gás de proteção a mistura 8% CO2 + 92% Ar. Quanto à redução e controle das distorções, três técnicas são utilizadas. A técnica que utiliza em escoadouro dinâmico de calor, formado por um jato de gás refrigerador aplicado logo após o arco de solda durante a soldagem, apresentou maior eficiência na redução das distorções, provenientes do ciclo térmico.
Título en inglés
Gas metal arc welding of thin sheet steels
Palabras clave en inglés
Distortion
Galvanized steel
Thin sheet
Welding
Resumen en inglés
The thin sheet steels, coated or not, has been widely used nowadays, mainly the hot dip galvanized steel sheets. It's observed as in the mechanic and automobilist industry as in the civil construction that in manufacturing of pieces and structures employ welding procedures. The aim of this work is to establish procedures to gas metal are welding with short circuit transfer of thin sheet steel elements, not coated and zinc-coated steel, in order to get junctions of acceptance quality and reduction of welding stress and distortion. This distortion arise of the thermal cycles that occur during the welding. In terms of the weld quality is defined the best consumables combination available in the market, in such a way to reduce the weld defects like porosities, spatters, cracks and loss of covering. To galvanized steel sheets, the combination: wire ER70S-3 and mixture 8%CO2 + 92% Ar showed the best performance. Three techniques were employed for control and reduce the welding distortion. One that using a spot heat sink following the arc, in this case the cooling jet, was more efficient that others techniques.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-09-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.