Disertación de Maestría
DOI
https://doi.org/10.11606/D.88.2016.tde-15092016-123234
Documento
Autor
Nombre completo
Luis Gustavo Sandrin Toscano
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1997
Director
Tribunal
Gomes, Samuel Irati Novaes (Presidente)
Crnkovic, Ovídio Richard
Ishikawa, Tomaz Toshimi
Título en portugués
Efeito da diluição da chapa base na soldagem com adição de pó de ferro utilizando fluxo experimental
Palabras clave en portugués
Adição de pó de ferro
Cordão de solda cobre-cromo-níquel
Cordão de solda nióbio-vanádio
Ensaios mecânicos de dureza-tração-impacto
Soldagem por arco submerso
Resumen en portugués
Neste trabalho foi feito o estudo sobre o efeito de elementos microligantes na composição química, microestrutura e propriedades mecânicas de metais como soldado produzidos por arco submerso com adição de pó de ferro em aço de alta resistência e baixa liga (ARBL). Foram feitos dois cordões de solda utilizando os aços BS - 4360 - 50 e USI - SAC - 50, o arame EM - 12K, o pó de ferro ESAB 400 e o fluxo experimental 10.71P. Utilizando-se a corrente de 600 A, tensão de 34 V, velocidade de soldagem de 30 cm/min e vazão de pó de ferro de 6,7 Kg/h foram produzidos os metais como soldado com um único passe e chanfro em "V", que mostraram características de boa temperabilidade e estrutura refinada. O microconstituinte em maior porcentagem nos dois cordões de solda foi a ferrita acicular. Os ensaios mecânicos realizados foram a dureza, tração e impacto. O cordão de solda com nióbio e vanádio obteve maiores valores de dureza e resistência à tração em relação ao cordão com cobre, cromo e níquel. Entretanto os altos teores de manganês presentes fizeram com que o endurecimento por solução sólida reduzisse significativamente a resistência ao impacto dos dois cordões de solda. A natureza das inclusões não metálicas foi investigada por microscopia eletrônica e análise por EDAX.
Título en inglés
not available
Palabras clave en inglés
Iron powder addition
Mechanical tests of hardness-tensile strength-impact
Submerged arc welding
Weld metal copper-chromium-nickel
Weld metal niobium-vanadium
Resumen en inglés
The study of the effect of microalloying elements in the chemical composition, microstructure and mechanical properties of the as-welded metaIs obtained by submerged are welding with iron powder addition in High Strength Low Alloy (HSLA) steel were done. Two weld metaIs were made using, BS - 4360 - 50 and USI - SAC - 50 steels, EM - 12K wire, ESAB 400 iron powder and 10.71P experimental flux. Using welding current of 600 A, arc voltage of 34 V, travel speed of 30 cm/min and iron powder flow of 6,7 Kg/h were obtained as-welded metals by single pass into V - groove, that showed good hardenability and refined microstructure. The higher percentage microstructure in the two weld metals was the acicular ferrite. The mechanical tests done were hardness, tensile strength and impact. The weld metal with niobium and vanadium achieve better values of hardness and yield strength than with copper, chromium and nickel weld metal. However, the hardening by solid solution, induced by the high levels of manganese, decreased the impact strength of the two weld metaIs. The non - metallic inclusions nature was investigated by electronic microscopy and EDAX analysis.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-09-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.