Mémoire de Maîtrise
DOI
10.11606/D.88.2016.tde-14092016-164116
Document
Auteur
Nom complet
Alessandro Fraga Farah
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1997
Directeur
Jury
Canale, Lauralice de Campos Franceschini (Président)
Bose Filho, Waldek Wladimir
Zavaglia, Cecília Amélia de Carvalho
Titre en portugais
Desenvolvimento de uma liga de ferro fundido branco alto cromo com nióbio, tratada termicamente, para resistência ao desgaste abrasivo
Mots-clés en portugais
Desgaste abrasivo
Ferro fundido branco
Revestimento duro
Tratamento térmico
Resumé en portugais
No presente trabalho são relatados os resultados obtidos através de tratamentos térmicos e de ensaios de abrasão, em uma liga de ferro fundido branco alto cromo contendo nióbio, obtida por fundição. Os tratamentos térmicos de têmpera foram efetuados nas temperaturas de 950, 1000, 1050 e 1100ºC e o meio de resfriamento utilizado foi o ar soprado. Os tratamentos de revenidos foram efetuados nas temperaturas de 450, 500 e 550ºC. A liga no estado termicamente tratado foi comparada, nos ensaios de abrasão, com ligas comerciais utilizadas como revestimento duro por soldagem em peças desgastadas. Os ensaios de abrasão do tipo pino sobre lixa. Adicionalmente, também foram efetuados estudos de caracterização microestrutural para a identificação das diferentes fases presentes nas ligas. De maneira geral, a liga estudada apresentou as melhores taxas de desgaste para os tratamentos térmicos que resultaram em maiores durezas e o seu desempenho foi superior ao das ligas comerciais.
Titre en anglais
Development of the white cast iron with niobium alloy, heat treating, to wear of the abrasive resistance
Mots-clés en anglais
Abrasive wear
Hardfacing
Heat treatment
White cast iron
Resumé en anglais
This work presents the heat treatments and abrasion tests results of a wnite cast iron with niobium alloy. The hardening heat treatment were made from 950, 1000, 1050 and 1100°C temperatures cooled by forced air. The tempering treatment were made at 450, 500 and 550°C temperatures. The heat treating alloy were compared, in the abrasive tests, with commercial alloys used as hardfacing by welding process in wear pieces. The abrasion tests was realized in pin on disk test. Additional tests were carried out for microstructural characterization to identify the differents phases presents in the alloys. In a general way, the alloy studied showed the best wear rate for the heat treatments that resulted in higher hardness. Its performance was superior than that of the commercial alloys.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-09-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.