Tese de Doutorado
DOI
10.11606/T.88.2010.tde-06012011-212324
Documento
Autor
Nome completo
Seila Rojas de Souza
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2010
Orientador
Banca examinadora
Hernandes, Antonio Carlos (Presidente)
Araújo, Eudes Borges de
Ferreira, Eduardo Bellini
Li, Maximo Siu
Ziemath, Ervino Carlos
Título em português
Propriedades térmicas, estruturais e ópticas de vidros germanatos de bismuto e sua cristalização abaixo da temperatura de transição vítrea
Palavras-chave em português
Cristalização abaixo de Tg
Espectroscopia de Absorção no Infravermelho
Espectroscopia Micro-Raman
Vidros germanatos de bismuto
Resumo em português
Materiais vítreos com propriedades similares às do cristal germanato de bismuto de composição Bi4Ge3O12, material cintilador que possui estrutura do tipo eulitita, são de interesse devido as suas propriedades luminescentes, que os tornam promissores para aplicação como dispositivos ópticos. Vidros do sistema GeO2-Bi2O3 (BGO) também tem sido tema de inúmeras pesquisas por combinarem um típico formador vítreo (GeO2) a um formador condicional composto intermediário (Bi2O3), o que os proporciona características estruturais únicas, resultantes da mudança de coordenação dos átomos de germânio (fenômeno de anomalia do germânio) e também dos átomos de bismuto. Neste trabalho, estudou-se a influência da adição de CeO2, comumente conhecido como agente oxidante, nas propriedades físico-químicas de vidros de germanato de bismuto do sistema [100-x].[(1-y)GeO2-yBi2O3]:xCeO2 (para x = 0,2 ou 1 e y = 0,2 ou 0,3 % em mol), preparados pelo método de fusão e moldagem. O escurecimento inomogêneo das amostras, associado à termoredução do íon Bi3+, foi evitado com a adição de céria, que se mostrou um modificador da estrutura local dos vidros, mesmo para uma dopagem de 0,2 % em mol. Foi observada, pela primeira vez, a cristalização da fase de estrutura eulitita cintiladora induzida pela presença de Ag na superfície do vidro de composição 99,8[0,8GeO2- 0,2Bi2O3 ]:0,2CeO2 % em mol, referido pela sigla 80BGO:0,2Ce, abaixo da temperatura de transição vítrea (Tg). A difusão de Ag no vidro é condição necessária para que o fenômeno da cristalização aconteça, uma vez que esse elemento pode ser considerado um efetivo agente nucleante para a fase cintiladora. A cristalização induzida é favorecida pela tensão gerada na interface cristal/vidro, devido a uma diferença de volume molar entre essas duas fases, o que permite que o fenômeno da cristalização seja observado em temperturas inferiores à Tg.
Título em inglês
Thermal, structural and optical properties of bismuth germanate glasses and their crystallization below the glass transition temperature
Palavras-chave em inglês
Bismuth-germanate glasses
Crystallization below Tg
Infrared Absorption Spectroscopy
Micro-Raman Spectroscopy
Resumo em inglês
Glassy materials with similar properties to those of the bismuth-germanate crystal in the composition of Bi4Ge3O12, a scintillator material with the eulytite structure, are of interest due to their luminescent properties that makes them promising materials to application as optical devices. Glasses from the system GeO2-Bi2O3 (BGO) has also being subjects of numerous studies, by combining a typical glass former oxide (GeO2) with the conditional one intermediate compound (Bi2O3). The presence of these two oxide compounds in the glass composition provides them a unique structural characteristic resulting from the coordination changes of germanium atoms (germanium anomaly phenomenon) and also of the bismuth atoms. In the present work, it was studied the influence of CeO2 addition, commonly known as an oxidant agent, in the physical-chemical properties of the bismuth-germanate glasses up to the system [100-x].[(1-y)GeO2-yBi2O3 ]:xCeO2 (for x = 0.2 or 1 and y = 0.2 or 0.3 mol %), prepared by the melting/molding method. The inhomogeneous darkening of the samples, associated to the thermal reduction of the Bi3+ ions, was avoided by the ceria addition that acts as a local modifier of the glass structure even for concentrations of 0.2 mol %. It was observed, by the first time, the crystallization of the eulytite scintillator phase, induced by the presence of Ag in the surface of the glass in the 99[0.8GeO2- 0.2Bi2O3 ]:0.2CeO2 mol % composition, referred to as 80BGO:0.2Ce, below the glass transition temperature (Tg). The Ag diffusion into the glass is a necessary condition to the crystallization phenomenon since this element can be considered as an effective nucleating agent to the scintillator phase. The crystallization is favored by the tension generated in the crystal/glass interface, due to a difference in molar volume of these two phases, allowing that the crystallization phenomenon be observed at temperatures below Tg.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2011-01-31
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.