Master's Dissertation
DOI
10.11606/D.88.2007.tde-04092008-163946
Document
Author
Full name
Danilo Borges Villarino de Castro
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2007
Supervisor
Committee
Bose Filho, Waldek Wladimir (President)
Baptista, Carlos Antonio Reis Pereira
Colosio, Marco Antonio
Title in Portuguese
Influência da temperatura de austenitização para têmpera e de revenimento na tenacidade e na vida em fadiga do aço SAE 5160 para diferentes teores de fósforo
Keywords in Portuguese
Aço SAE 5160
Austenitização
Fósforo
Fragilização
Revenimento
Abstract in Portuguese
O objetivo deste trabalho foi investigar a influência das temperaturas de austenitização de têmpera e de revenimento na tenacidade ao impacto e na vida em fadiga do aço-mola SAE 5160, considerando diferentes teores de fósforo. Foram efetuados tratamentos térmicos de têmpera e revenimento em lâminas de aço SAE 5160 com bitolas de 70x10 mm, utilizando três diferentes temperaturas de austenitização: 850ºC, 900ºC, e 1000ºC, com tempo de permanência em forno durante 15 minutos. A temperatura do óleo de têmpera foi de 66ºC. As condições de revenimento foram de 470ºC (70 min), 500ºC (64 min), e 530ºC (59 min), desde que a dureza final fosse mantida no intervalo de 45±3 HRC. Foram efetuados tratamentos térmicos em lâminas com baixo, médio e altos teores de fósforo (0,012%, 0,017%, 0,025% e 0,031% em peso), com a finalidade de observar o efeito do teor de fósforo sobre uma possível fragilização do aço-mola. Analisando os resultados obtidos, foi possível observar que o P, mesmo em teores abaixo do máximo permitido e dependendo das temperaturas de austenitização e revenido, pode causar a fragilização induzindo à fratura frágil do tipo intergranular, como foi observado nas análises das superfícies de fratura. No entanto, se a vida de nucleação for considerada, pode-se observar também que a fragilização não possui efeito algum sobre a vida em fadiga do componente.
Title in English
The Influence of the Austenitizing Temperatures for Quenching and Tempering on the Toughness and Fatigue Life of SAE 5160 Steel with Different P Contents
Keywords in English
5160 steel
Austenitizing
Phosphorus
Temperin
Abstract in English
The aim of this work was to analyze the influence of austenitizing and tempering temperatures on the impact and fatigue life of the SAE 5160 spring steel, considering two different P amount. Bars (70 x 10 mm) were heat treated using three different austenitizing temperatures, 850ºC, 900ºC and 1000ºC, with a 15 min furnace soaking time. The quenching temperature was 66ºC. The tempering conditions were 470ºC (70 min), 500ºC (64 min), e 530ºC (59 min), since the final hardness has to be kept in the range of 45±3 HRC. Heat treatment was carried out in materials with similar chemical compositions but with different P levels, this is, 0,012%, 0,017%, 0,025% and 0,031 wt%, looking at the effect of the P level to quench and temper embrittlement. From the results was possible to observe that the P content, even bellow the maximum level, depending on the quench and temper temperatures may cause embrittlement, as observed by the absorbed impact energy and fracture surface analysis. However, if nucleation life is considered, it was also observed that this embrittlement has no effect on the fatigue life.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2008-09-12
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.