Dissertação de Mestrado
DOI
10.11606/D.88.1998.tde-02072003-093007
Documento
Autor
Nome completo
André Luís Paschoal
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1998
Orientador
Banca examinadora
Canale, Lauralice de Campos Franceschini (Presidente)
Andreeta, Jose Pedro
Higa, Olga Zazuco
Título em português
Avaliação da resistência à corrosão em meio fisiológico de metais revestidos com nitreto de titânio.
Palavras-chave em português
biomateriais metálicos
nitreto de titânio
revestimento
Resumo em português
Metais são bastante usados como materiais implantáveis, principalmente para dispositivos feitos na área de ortopedia. Há uma constante relação dos processos de corrosão nesse biomateriais com a agressividade do meio fisiológico. Usando quatro tipo de metais e ligas metálicas – titânio puro, liga de titânio, aço inoxidável de baixo carbono e liga de cobalto – o processo de corrosão foi estudado. Além disso, o desempenho desses materiais revestidos com nitreto de titânio foi avaliado. Dois processos de revestimento por PVD – evaporação e magnetron sputtering – foram executados, verificando a eficiência desses materiais em meio fisiológico - O melhor comportamento se deu para o revestimento obtido por evaporação. O mecanismo de corrosão predominante para as amostras foi indicado.
Título em inglês
Evaluation of the resistance to the corrosion in physiologic environment of metals covered with titanium nitrite.
Palavras-chave em inglês
coating
metallic biomaterials
titanium nitrite
Resumo em inglês
Metals are very much used as implantable materials mainly for the construction of devices orthopaedic area. There is a constant concern about the corrosion process in those metallic biomaterials due to the aggressiveness of the physiological environment. By using four types of metals and metallic alloys – pure titanium, titanium alloy, low carbon stainless steel and cobalt-chromium alloy – the corrosion process in physiologic environment has been studied. Also, the performance of such materials coated with titanium nitrate was evaluated. Two PVD coating methods – evaporation and magnetron sputtering – were performed, and the efficiency of those materials in physiologic medium was verified. The best behaviour was found by the evaporation coating method. The predominant corrosion mechanism for coated samples was suggested.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
dissertandre.pdf (8.78 Mbytes)
Data de Publicação
2003-09-01
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.