Tese de Doutorado
DOI
10.11606/T.87.2008.tde-21012009-115422
Documento
Autor
Nome completo
Miriam Lúcia Chiquetto Machado
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2008
Orientador
Banca examinadora
Pradella, Jose Geraldo da Cruz (Presidente)
Bonomi, Antonio Maria Francisco Luiz José
Gouvêa, Míriam Tvrzská de
Hokka, Carlos Osamu
Kilikian, Beatriz Vahan
Título em português
Estudos das propriedades mecânicas e térmicas do polímero biodegradável poli-3-hidroxibutirato (PHB) e de compósitos PHB/pó de madeira.
Palavras-chave em português
Irradiação de materiais
Poli-3-hidroxibutirato
Processamento de materiais
Propriedades mecânicas
Propriedades térmicas
Resumo em português
O objetivo deste trabalho foi o estudo das propriedades mecânicas e térmicas do PHB e de compósitos de PHB/pó de madeira processados, reprocessados e irradiados. Foram preparados compósitos com PHB e pó de madeira com concentrações de PHB/pó de madeira de 90/10, 80/20 e 70/30 (m/m). Foram realizados ensaios de propriedades mecânicas, HDT, ponto de amolecimento Vicat, TGA e DSC. A incorporação do pó de madeira aumentou o grau de cristalinidade e a temperatura de cristalização do polímero, e nos compósitos PHB/pó de madeira 80/20 e 70/30 a rigidez do material aumentou em relação ao polímero puro. O compósito PHB/pó de madeira 70/30 apresentou os melhores resultados em termos econômicos, de processamento e de estabilidade em relação ao reprocessamento. A irradiação após o processamento, em dose de 30 kGy, provocou aumento da rigidez do PHB puro e dos compósitos PHB/pó de madeira 90/10 e 80/20, embora as outras propriedades tenham decrescido. O compósito PHB/pó de madeira 70/30 apresentou queda de todas as propriedades com a irradiação.
Título em inglês
Study of mechanical and thermal properties of the biodegradable polymer poly-3-hydroxybutyrate (PHB) and PHB/wood flour composites.
Palavras-chave em inglês
Materials irradiation
Materials processing
Mechanical properties
Poly-3-hydroxybutyrate
Thermal properties
Resumo em inglês
The purpose of this work was the study of the mechanical and thermal properties of processed, reprocessed and irradiated PHB, as well as PHB/wood flour composites. PHB/wood flour composites were prepared with PHB/wood relation of 90/10, 80/20 e 70/30 (w/w). Mechanical properties, HDT, Vicat melting point and thermo analyses (TGA and DSC) tests were carried out. The introduction of the wood flour increased both polymer crystallinity and crystallization temperature. The material stiffness increased in PHB/wood flour composites (80/20 and 70/30) resulting in higher values in some properties when compared with pure PHB. The PHB/wood flour composite 70/30 showed the best results in terms of economy, processing and stability during reprocessing. The irradiation after processing in 30kGy doses led to a stiffness increasing of pure PHB and PHB/wood flour composites (90/10 and 80/20) while other properties have decreased. The PHB/wood flour 70/30 showed decreasing in all properties after irradiation.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2009-03-19
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.