Dissertação de Mestrado
DOI
10.11606/D.85.2015.tde-28082015-103250
Documento
Autor
Nome completo
Arthur Maximo
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2015
Orientador
Banca examinadora
Rossi, Wagner de (Presidente)
Berretta, José Roberto
Riva, Rudimar
Título em português
Comparação entre soldagem de chapas finas de tântalo e monel 400 com laser pulsado de Nd:YAG e com laser contínuo de fibra
Palavras-chave em português
chapas finas
corrosão
Monel
soldagem a laser
Tântalo
Resumo em português
Neste trabalho foram realizados experimentos de soldagem de chapas de Tântalo e Monel 400 com 100 m de espessura. Foram realizadas soldas em um laser de Nd:YAG operando em modo pulsado e em um Laser de Fibra operando em modo contínuo. Em seguida a microestrutura das amostras foram analisadas através de microscopia ótica e foram realizados ensaio de microdureza Vickers. As amostras que apresentaram melhores resultados foram submetidas a ensaios de tração e a ensaios de corrosão. Após análise dos resultados observou-se que a soldagem a laser apresenta muitos benefícios em relação a outros processos convencionais para chapas finas. A soldagem no modo pulsado apresentou maior relação de aspecto se comparado a soldagem em modo contínuo. A soldagem em modo contínuo apresentou uma velocidade de soldagem muito superior ao modo pulsado. Os resultados indicaram que a soldagem no modo pulsado apresenta maior aplicabilidade para chapas finas, devido à necessidade um controle preciso sobre a intensidade aplicada.
Título em inglês
Comparison between welding of thin sheets of Tantalum and Monel 400 with pulsed Nd:YAG laser and continuous fiber laser
Palavras-chave em inglês
corrosion
laser welding
Monel
tantalum
thin sheets
Resumo em inglês
This work carried out welding experiments of Tantalum and Monel 400 plates with 100 mm thickness. Welds were made with an Nd: YAG laser operating in a pulsed mode and in a fiber laser operating in continuous mode. Then the microstructure of the samples were analyzed by optical microscopy and were performed Vickers microhardness test. Samples that showed better results were subjected to tensile tests and the corrosion tests. After analysis of the results showed that the laser welding offers many benefits over other conventional processes for thin sheets. The welding in pulsed mode presented in superior aspect ratio compared to welding in continuous mode. The welding in continuous mode showed a much higher welding speed to pulsed mode. The results indicated that the welding in pulsed mode shows more applicability for sheet metal, due the need of a precise control of applied intensity.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2015-08-31
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.