Tesis Doctoral
DOI
https://doi.org/10.11606/T.85.2006.tde-28062007-123420
Documento
Autor
Nombre completo
Edson Souza de Jesus Filho
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2005
Director
Tribunal
Rossi, Jesualdo Luiz (Presidente)
Ambrozio Filho, Francisco
Gomes, Edson
Robert, Maria Helena
Vatavuk, Jan
Título en portugués
"PROCESSAMENTO, USINAGEM E DESGASTE DE LIGAS SINTERIZADAS PARA APLICAÇÕES AUTOMOTIVAS"
Palabras clave en portugués
aço rápido
automotivo
cobalto
desgaste
ferro
inserto para assento de válvula
metalurgia do pó
motor de combustão interna
sinterização
tratamento térmico
usinabilidade
usinagem
Resumen en portugués
O objetivo deste trabalho foi desenvolver potenciais materiais para aplicações automotivas, em particular como insertos para assento de válvula em motores de combustão interna à gasolina. O desenvolvimento compreendeu as etapas de processamento dos materiais via metalurgia do pó, tratamento térmico, caracterização microestrutural e mecânica, usinagem e desgaste dos mesmos. O desenvolvimento objetivou principalmente a redução de custo e a aplicação de elementos menos poluentes, excluindo-se, por exemplo, a aplicação do Co devido ao seu alto custo e do Pb devido aos seus efeitos toxicológicos e prejudiciais ao meio ambiente. A realização de uma pesquisa minuciosa na busca de patentes relacionadas indicou que os materiais estudados apresentam composições particulares, e, portanto inéditas. Os resultados encontrados nos ensaios de dureza e de resistência à compressão radial nas amostras tratadas termicamente apresentaram resultados superiores aos da liga comercial atualmente em uso. Testes de usinabilidade em amostras sem tratamento térmico apresentaram comportamento similar ao da liga comercial, indicando que a usinabilidade do material praticamente não foi afetada com a mudança na composição química. Após a etapa de tratamento térmico, as ligas obtidas apresentaram valores de esforços de corte superiores aos do material comercial. Os resultados dos testes de desgaste abrasivo em amostras tratadas termicamente apresentaram menores valores de coeficientes de atrito e perda de massa em todos os casos em relação ao material comercial. Este comportamento é devido aos benefícios introduzidos pelo tratamento térmico executado e pela adição de alguns elementos resistentes ao desgaste na forma de carbonetos de Nb e Ti/W. Os resultados dos esforços de corte apresentaram boa concordância com os resultados dos ensaios de desgaste. Os materiais produzidos apresentam-se como potenciais candidatos para substituir, com vantagens, inserto para assento de válvula a base de Fe-Co em motores de combustão interna a gasolina.
Título en inglés
"OBTENTION, MACHINING AND WEAR OF SINTERED ALLOYS FOR AUTOMOTIVE APPLICATIONS"
Palabras clave en inglés
automotive
cobalt
ferrous
heat treatment
high speed steel
internal combustion engine
machinability
machining
powder metallurgy
sintering
valve seat insert
wear
Resumen en inglés
The aim of this work was the development of materials for automotive applications, in particular, valve seat inserts for gasoline combustion engines. The development involved the following activities: processing by powder metallurgy techniques, heat treatment, mechanical and microstructural characterization, machining and wear of materials. This work was undertaken aiming cost reduction of this component by the use of cheaper and less pollutant elements, eliminating the presence of Co and Pb due to their high cost and toxicological effects, respectively. The accomplishment of a thorough research into patents revealed that the materials studied here present particular compositions and were not yet produced. The results of hardness measurements and the transverse radial strength of the studied materials, after heat treatment, revealed superior properties than the commercial alloys applied at the moment. The machining tests of the material without heat treatment indicated a similar behaviour in comparison to the commercial alloy, suggesting that the new alloy chemistry composition was not deleterious in this sense. After heat treatment, the obtained alloys presented a cutting force increase in relation to the commercial alloy. Wear tests results of heat treated materials presented smaller friction coefficient and mass loss than the commercial alloy, in all cases. This was especially achieved due to the advantages offered by heat treatment allied to the addition of NbC and Ti/W carbides. The materials obtained here showed to be potential candidates to substitute with advantages, valve seat inserts made of Fe-Co alloys for gasoline combustion engines.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
TeseEdson.pdf (12.38 Mbytes)
Fecha de Publicación
2007-09-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.