• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.85.2014.tde-28012015-150337
Documento
Autor
Nombre completo
Igor Passos dos Santos
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2014
Director
Tribunal
Rossi, Jesualdo Luiz (Presidente)
Colosio, Marco Antonio
Jesus, Edilson Rosa Barbosa de
Título en portugués
Processamento e caracterização de aços sinterizados para uso em insertos de assentos de válvulas
Palabras clave en portugués
aço rápido
inserto de asserto de válvula
metalurgia do pó
Resumen en portugués
O objetivo deste trabalho foi propor potenciais misturas de pós para utilização na indústria automotiva, mais especificamente ligas metálicas aplicadas na produção de insertos de assentos de válvulas. A pesquisa foi dividida em etapas como segue a produção via metalurgia do pó: seleção dos componentes para as ligas metálicas estudadas, aquisição e preparo de cada um dos pós metálicos, caracterização física e microscópica dos componentes da mistura, definição das proporções a serem usadas, mistura dos pós constituintes, compactação a frio em prensa uniaxial, sinterização das peças de acordo com ciclo térmico e atmosfera específicos, realização de ensaios de dureza, resistência à compressão radial e análise microestrutural por microscopia de varredura eletrônica. As misturas de pós forma basicamente pó de ferro misturado com aços rápidos, AISI M3/2, D2 e M2. Os insertos produzidos com a liga metálica denominada M3/2 mostraram-se mais vantajosos em relação aos demais por terem apresentado melhor desempenho nos testes de dureza e resistência à compressão radial.
Título en inglés
Processing and characterization of sintered steel for use in valve seat inserts
Palabras clave en inglés
poder metallurgy
speed steel
valve insert assent
Resumen en inglés
The aim of this study was to propose potential materials for use in the automotive industry, specifically alloys applied in the production of valve seat inserts. The research was divided in steps according to standard powder metallurgy technique: selecting components for the studied alloys, acquisition and preparation of each of the metal powders, physical and microscopic characterization of the components, defining the proportions to be used, a mixture of alloys, compaction in uniaxial presses, sintering the parts according to thermal cycle and specific atmosphere, hardness tests, resistance to radial compression and microstructural analysis using scanning electron microscopy. The powders mixtures were basically iron powder mixed with high-speed steels type AISI M3/2, D2 and M2. The valve seat inserts made with the alloy M3/2 showed to be more advantageous in relation to the other mixtures in terms of hardness and transverse rupture strength.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-03-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.