Master's Dissertation
DOI
https://doi.org/10.11606/D.85.2011.tde-25082011-151614
Document
Author
Full name
Railson Bolsoni Falcão
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2011
Supervisor
Committee
Leal Neto, Ricardo Mendes (President)
Rocha, Claudio Jose da
Vatavuk, Jan
Title in Portuguese
Obtenção do TiFe por moagem com alta energia
Keywords in Portuguese
compostos intermetálicos
elaboração mecânica
moagem com alta energia
Abstract in Portuguese
Neste trabalho, investigou-se a elaboração mecânica do composto intermetálico TiFe por moagem de bolas com alta energia. Uma forte aderência do material moído, particularmente nas paredes do recipiente de moagem, foi o principal problema verificado com tempos de moagem superiores a 1 hora (moinho agitador). Tentativas para resolver este problema foram realizadas inicialmente com o emprego de agentes controladores de processo (ACPs), como etanol, ácido esteárico, polietileno de baixa densidade, benzeno e ciclohexano, em diferentes quantidades (1 a 20% em massa) e tempos (1 a 40 h), mantendo-se constantes outros parâmetros de moagem como a razão bola:pó em massa (10:1) e o tamanho das bolas (=7mm). Os rendimentos mais elevados (em termos da massa de pó não aderido) foram obtidos quando se utilizaram grandes quantidades de benzeno e ciclohexano (101 e 103% em massa, respectivamente), porém com a formação de TiC ao invés de TiFe em razão da decomposição do ACP e reação do carbono com as partículas de titânio. As moagens foram realizadas posteriormente sem o emprego de qualquer ACP e também utilizando um moinho planetário. Várias estratégias foram investigadas para se tentar mitigar a aderência incluindo-se: (a) moagem de uma pequena quantidade da mistura de pós de Ti e de Fe, revestindo as paredes do recipiente e as bolas de moagem, antes da moagem da carga principal, (b) moagem pausada com aberturas intermediarias do recipiente em atmosfera ambiente, (c) moagem pausada para rotação e inversão da posição do recipiente de moagem (apenas no moinho agitador), (d) moagem isolada dos pós de Ti e de Fe, antes da moagem da mistura, e (e) moagem do pó de Fe com o Ti hidretado. Os melhores resultados, em termos de diminuição da aderência combinada com a formação majoritária do composto TiFe durante a moagem, foram obtidos quando se adotou o procedimento de inversão/rotação, juntamente com o processo de revestimento preliminar do recipiente e das bolas de moagem (26% em massa). Rendimentos maiores foram obtidos com a utilização do TiH2 no moinho planetário, porém sem a formação majoritária do TiFe durante a moagem.
Title in English
Obtention of TiFe by high-energy ball milling
Keywords in English
high-energy ball milling
intermetallic compound
mechanical alloying
Abstract in English
In this work an investigation on the mechanical alloying of the intermetallic compound TiFe by high-energy ball milling was conducted. Strong adherence of milled material, particularly at the vial walls, was seen to be the main problem at milling times higher than 1 hour (shaker mill), hindering the compound synthesis. Attempts to prevent this problem were accomplished first by adding different process control agents (PCAs), like ethanol, stearic acid, low density polyethylene, benzene and cyclohexane at variable quantities (1 to 20 wt. %) and times (1 to 40 h), keeping constant other milling parameters like ball to powder mass ratio (10:1) and balls size (=7mm). Highest yields (related to the non adhered powder) were attained with larger amounts of benzene and cyclohexane (101 and 103 wt. %, respectively), but with TiC formation during milling instead of TiFe due to the PCA decomposition and the reaction of the carbon with and titanium particles. Milling was conducted further without adding any PCA and also using a planetary ball mill. Several strategies were tried to avoid or minimize the adherence including: (a) milling of a small quantity of the Ti and Fe powder mixture, dirtying the vial walls and the balls surfaces before milling the main charge, (b) stepwise milling with intermediate openings of the vial in air, (c) stepwise milling with the rotation and the inversion of the vial position between the steps (only in the shaker mill), (d) milling Ti and Fe powders (apart from each other) before milling the mixture of them, and (e) milling Fe powder with Ti hydride powder. Best results concerning both yield and major TiFe formation during milling were verified with the rotation/inversion procedure combined with preliminar dirtying of the vial and balls (26 wt.% in the shaker mill). Higher yields could be attained by using TiH2 powder in the planetary mill, but with no major TiFe formation during milling.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-08-31
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.