• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
10.11606/D.85.2009.tde-22092011-101543
Document
Auteur
Nom complet
Leonardo Calicchio
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2009
Directeur
Jury
Pillis, Marina Fuser (Président)
Ambrozio Filho, Francisco
Vatavuk, Jan
Titre en portugais
Efeito do 'shot peening' sobre a nitretação de peças de ferro produzidas por metalurgia do pó
Mots-clés en portugais
metalurgia do pó
nitretação
shot peening
Resumé en portugais
Atualmente, quando se tem a necessidade de nitretar peças produzidas pela metalurgia do pó, usa-se a nitretação a plasma. Apesar de ser um processo de alto custo, com diversas dificuldades operacionais e de ajuste de processo, a nitretação a plasma é o único processo viável para nitretar esses materiais por ter uma ação apenas superficial, não apresentando ação nitretante no interior dos poros. Nos processos de nitretação a gás e banho de sais, o meio nitretante penetra na porosidade (interconectada) dos materiais sinterizados, havendo assim a formação de camada branca em uma grande profundidade da peça (ou mesmo na peça toda), gerando problemas de deformação e fragilização do componente. Este trabalho teve por objetivo a aplicação do processo shot peening em peças sinterizadas com a finalidade de fechar a porosidade superficial das peças e estudar seu comportamento sob o processo de nitretação a gás. O estudo verifica que o material sinterizado submetido à nitretação gasosa permitiu a entrada do meio nitretante pelos poros abertos e interconectados promovendo a formação de camada branca no interior dos poros de praticamente todo o volume da peça. Essa camada branca no interior do material fragiliza o componente e inviabiliza sua utilização como componente em praticamente qualquer aplicação industrial. As peças sinterizadas jateadas com granalhas de aço antes da nitretação também permitiram o acesso do meio nitretante no interior do componente, porém, sem potencial suficiente para a formação de camada branca. As amostras jateadas apresentaram apenas agulhas de nitretos formados durante a nitretação.
Titre en anglais
The effect of shot peening on the gas nitriding of iron components produced by powder metallurgy
Mots-clés en anglais
iron
iron nitrides
nitridation
nitrogen compounds
powder metallurgy
shot peening
surface treatments
Resumé en anglais
Plasma nitriding is the process used to nitriding components produced by powder metallurgy. Although its high coast and operational difficulties, this is the best process for this kind of materials because the nitring occurs only in the surface. In gas and liquid nitriding processes the nitriding atmosphere goes through interconnected porous and the white layer forms not only on the surface but around internal porous resulting in embrittlement and deformation of the component. The aim of this work was evaluate the gas nitriding behavior of iron samples as received and previously submitted to shot peening process in order to close superficial porosities in a gas nitriding process. The results have shown that during gas nitriding the samples as received, did not present white layer at the surface but around the porous in the bulk of the sample. This fact suggested that the gaseous atmosphere goes through interconnected porous. This white layer causes the embrittlement of the component and its use in industrial application is not recommended. Otherwise, samples previously submitted to shot peening process before nitriding showed an external white layer but also permitted the access of nitriding atmosphere to the bulk of the sample, but in this case the nitriding potential was not sufficient to form white layer around internal porous.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-07-23
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.