Disertación de Maestría
DOI
10.11606/D.85.2016.tde-19042016-103336
Documento
Autor
Nombre completo
Bianca Alves Marcello
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Pillis, Marina Fuser (Presidente)
Lazar, Dolores Ribeiro Ricci
Sayeg, Isaac Jamil
Título en portugués
Caracterização microestrutural, morfológica e fotocatalítica de filmes finos de TiO2 obtidos por deposição química de organometálicos em fase vapor
Palabras clave en portugués
deposição química de organometálicos em fase vapor
dióxido de titânio
fotocatálise
Resumen en portugués
O dióxido de titânio possui diversas aplicações tecnológicas, desde pigmento em tintas, até revestimentos funcionais. É um material resistente à degradação eletroquímica e fotoquímica. Com o aumento da produção industrial de corantes, há um aumento significativo da produção de rejeitos, sendo necessário o desenvolvimento de novas técnicas de degradação, a fim de reduzir a formação de efluentes. Dentre essas técnicas encontram-se os processos oxidativos avançados (POAs), que se baseiam na formação de radicais hidroxila para a degradação dos compostos liberados nos efluentes. A fotocatálise heterogênea utiliza um material semicondutor ativado por radiação ultra-violeta a fim de produzir os radicais hidroxila. Apesar de existirem estudos relacionados à utilização do TiO2 como fotocatalisador, há poucos dados com relação à sua aplicação na forma de filme suportado. Este trabalho teve por objetivos crescer filmes de TiO2 sobre borossilicato, por meio da técnica de deposição química de organometálicos em fase vapor, nas temperaturas de 400 e 500ºC por até 60 minutos, bem como proceder à caracterização microestrutural, morfológica e fotocatalítica desses filmes. Anatase foi a fase identificada em todos os filmes. Os filmes crescidos a 400°C apresentaram estrutura densificada, enquanto que os filmes crescidos a 500°C apresentaram estrutura colunar bem definida. A fotodegradação foi avaliada por meio da degradação do corante alaranjado de metila nos valores de pH 2,00; 7,00 e 10,00. Os resultados de degradação do corante mostraram que a maior eficiência do processo de degradação ocorre em pH = 2. Nessa condição, os melhores resultados ocorrem com o filme crescido por 30 minutos a 400°C, que apresentou 65,3% de degradação.
Título en inglés
Microstructural, morphologic and photocatalytic characterization of TiO2 thin films grown by metalorganic chemical vapor deposition
Palabras clave en inglés
metalorganic chemical vapor deposition
photocatalytic
titanium dioxide
Resumen en inglés
Titanium dioxide has many technological applications, as pigment in paints, and functional coatings. It is resistant to electrochemical and photochemical degradation. The increase of the industrial production of dyes results in a significant increase in production of wastes, which requires the development of new degradation techniques to reduce the release of effluents. Among these techniques there is the advanced oxidation process (AOP), which is based on the formation of hydroxyl radicals to the degradation of the compounds in the effluent released. The heterogeneous photocatalysis uses a semiconductor material activated by UV radiation to yield hydroxyl radicals. Although there are studies regarding the use of TiO2 as photocatalyst, there are few data related to its application in the form of supported film. The aim of this study was to grow TiO2 films on borosilicate substrate at 400 and 500°C for up to 60 minutes by using metallorganic chemical vapor deposition technique and proceed to the microstructural, morphology and photocatalytic characterization of the films. Anatase phase was identified in all films. The films grown at 400°C presented a densified structure, while the films grown at 500°C showed well defined columnar structure. The photodegradation was assessed by degradation of methyl orange dye in pH 2.00; 7.00 and 10.00. The results of dye degradation showed that the highest efficiency occurred at pH 2. In this condition, the best results occurred for the film grown for 30 minutes at 400°C and presented a degradation of 65.3%.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-05-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.