Master's Dissertation
DOI
10.11606/D.85.2016.tde-19042016-103336
Document
Author
Full name
Bianca Alves Marcello
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2015
Supervisor
Committee
Pillis, Marina Fuser (President)
Lazar, Dolores Ribeiro Ricci
Sayeg, Isaac Jamil
Title in Portuguese
Caracterização microestrutural, morfológica e fotocatalítica de filmes finos de TiO2 obtidos por deposição química de organometálicos em fase vapor
Keywords in Portuguese
deposição química de organometálicos em fase vapor
dióxido de titânio
fotocatálise
Abstract in Portuguese
O dióxido de titânio possui diversas aplicações tecnológicas, desde pigmento em tintas, até revestimentos funcionais. É um material resistente à degradação eletroquímica e fotoquímica. Com o aumento da produção industrial de corantes, há um aumento significativo da produção de rejeitos, sendo necessário o desenvolvimento de novas técnicas de degradação, a fim de reduzir a formação de efluentes. Dentre essas técnicas encontram-se os processos oxidativos avançados (POAs), que se baseiam na formação de radicais hidroxila para a degradação dos compostos liberados nos efluentes. A fotocatálise heterogênea utiliza um material semicondutor ativado por radiação ultra-violeta a fim de produzir os radicais hidroxila. Apesar de existirem estudos relacionados à utilização do TiO2 como fotocatalisador, há poucos dados com relação à sua aplicação na forma de filme suportado. Este trabalho teve por objetivos crescer filmes de TiO2 sobre borossilicato, por meio da técnica de deposição química de organometálicos em fase vapor, nas temperaturas de 400 e 500ºC por até 60 minutos, bem como proceder à caracterização microestrutural, morfológica e fotocatalítica desses filmes. Anatase foi a fase identificada em todos os filmes. Os filmes crescidos a 400°C apresentaram estrutura densificada, enquanto que os filmes crescidos a 500°C apresentaram estrutura colunar bem definida. A fotodegradação foi avaliada por meio da degradação do corante alaranjado de metila nos valores de pH 2,00; 7,00 e 10,00. Os resultados de degradação do corante mostraram que a maior eficiência do processo de degradação ocorre em pH = 2. Nessa condição, os melhores resultados ocorrem com o filme crescido por 30 minutos a 400°C, que apresentou 65,3% de degradação.
Title in English
Microstructural, morphologic and photocatalytic characterization of TiO2 thin films grown by metalorganic chemical vapor deposition
Keywords in English
metalorganic chemical vapor deposition
photocatalytic
titanium dioxide
Abstract in English
Titanium dioxide has many technological applications, as pigment in paints, and functional coatings. It is resistant to electrochemical and photochemical degradation. The increase of the industrial production of dyes results in a significant increase in production of wastes, which requires the development of new degradation techniques to reduce the release of effluents. Among these techniques there is the advanced oxidation process (AOP), which is based on the formation of hydroxyl radicals to the degradation of the compounds in the effluent released. The heterogeneous photocatalysis uses a semiconductor material activated by UV radiation to yield hydroxyl radicals. Although there are studies regarding the use of TiO2 as photocatalyst, there are few data related to its application in the form of supported film. The aim of this study was to grow TiO2 films on borosilicate substrate at 400 and 500°C for up to 60 minutes by using metallorganic chemical vapor deposition technique and proceed to the microstructural, morphology and photocatalytic characterization of the films. Anatase phase was identified in all films. The films grown at 400°C presented a densified structure, while the films grown at 500°C showed well defined columnar structure. The photodegradation was assessed by degradation of methyl orange dye in pH 2.00; 7.00 and 10.00. The results of dye degradation showed that the highest efficiency occurred at pH 2. In this condition, the best results occurred for the film grown for 30 minutes at 400°C and presented a degradation of 65.3%.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-05-06
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.