Disertación de Maestría
DOI
https://doi.org/10.11606/D.85.2011.tde-17062011-145032
Documento
Autor
Nombre completo
Luciana Ventavele da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Monteiro, Waldemar Alfredo (Presidente)
Andrade, Arnaldo Homobono Paes de
Buso, Sidnei José
Título en portugués
Estudos dos mecanismos envolvidos em processos de endurecimento superficial a laser de ligas a base de alumínio
Palabras clave en portugués
endurecimento superficial
liga Al-Si
microestrutura
Nd:YAG
propriedades mecânicas
Resumen en portugués
As ligas de Al-Si são amplamente utilizadas na indústria em substituição ao aço e o ferro fundido nos setores de alta tecnologia. A importância comercial dessas ligas deve-se principalmente ao seu baixo peso, excelente resistência à abrasão e à corrosão, alta resistência em temperaturas elevadas, baixo coeficiente de expansão térmica e menor consumo de combustível que proporciona redução considerável de emissão de poluentes. No presente trabalho, uma liga de Al-Si utilizada na indústria automobilística para fabricação de pistões de motores de combustão interna, foi submetida a tratamentos superficiais de refusão a LASER (Nd:YAG, λ = 1,06 m, modo pulsado). A radiação laser possibilita diversas concentrações de energia com precisa transferência dela para o material sem contato físico. A transferência intensa de energia provoca a ocorrência de modificações estruturais na camada superficial do material. Experimentos com pulsos únicos e trilhas foram realizados sob diferentes condições de processamento LASER com o intuito de analisar as mudanças microestruturais resultantes dos tratamentos e seus efeitos sobre a dureza. Para a caracterização da camada endurecida foram utilizadas as seguintes técnicas: microscopia óptica (MO), microscopia eletrônica de varredura (MEV), espectroscopia por energia dispersiva (EDS), mapeamento de raios-X, ensaios de microdureza Vickers e de rugosidade máxima. Após os tratamentos superficiais de refusão a LASER da liga Al-Si, a alta taxa de resfriamento resultante causou mudança na microestrutura devido ao refinamento das partículas de silício eutético primário presentes na liga, resultando em aumento de dureza.
Título en inglés
Studies of the mechanisms involved in the laser surface hardening process of aluminum base alloys
Palabras clave en inglés
Al-Si alloy
mechanical properties
Nd:YAG
Resumen en inglés
The Al-Si alloys are widely used in industry to replace the steel and gray cast iron in high-tech sectors. The commercial importance of these alloys is mainly due to its low weight, excellent wear (abrasion) and corrosion resistance, high resistance at elevated temperatures, low coefficient of thermal expansion and lesser fuel consumption that provide considerable reduction of emission of pollutants. In this work, Al-Si alloy used in the automotive industry to manufacture pistons of internal combustion engines, was undergone to surface treatments using LASER remelting (Nd:YAG, λ = 1.06 m, pulsed mode). The LASER enables various energy concentrations with accurate transfer to the material without physical contact. The intense energy transfer causes the occurrence of structural changes in the superficial layer of the material. Experiments with single pulses and trails were conducted under various conditions of LASER processing in order to analyze microestrutural changes resulting from treatments and their effects on the hardness. For the characterization of hardened layer was utilized the following techniques: optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), x-ray mapping, Vickers microhardness and maximum roughness tests. The high cooling rate caused a change in the alloy structure due to the refinement of the primary eutectic silicon particles, resulting in increase of the mechanical properties (hardness) of the Al-Si alloy.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2011SilvaEstudos.pdf (11.51 Mbytes)
Fecha de Publicación
2011-06-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.