Tesis Doctoral
DOI
https://doi.org/10.11606/T.85.2015.tde-16092015-102833
Documento
Autor
Nombre completo
Julio César Serafim Casini
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Takiishi, Hidetoshi (Presidente)
Ett, Gerhard
Leal Neto, Ricardo Mendes
Saeki, Margarida Juri
Wendhausen, Paulo Antônio Pereira
Título en portugués
Influência da substituição do cobalto por estanho e cobre na microestrutura e propriedades elétricas em ligas a base de LaMgAlMnCoNi
Palabras clave en portugués
baterias Ni-MH
ligas de estocagem de hidrogênio
ligas de LaNi5
terras raras
Resumen en portugués
Neste trabalho, avaliou-se inicialmente o efeito da substituição de elementos em ligas à base de LaMgAlMnCoNi do tipo AB5 com adição de estanho (Sn) e cobre (Cu) em substituição ao cobalto (Co), para utilização em ligas absorvedoras de hidrogênio e em eletrodos negativos de baterias de Ni-HM. Avaliou-se a influência desta substituição na microestrutura do material. Notou-se que o aumento da concentração de estanho promove a formação da fase LaNiSn nas ligas, bem como a diminuição das duas fases principais: LaNi5 e (La,Mg)Ni3. Adicionalmente, utilizou-se o refinamento de Rietveld para quantificar as fases em cada composição. Posteriormente, propôs-se um estudo da absorção de hidrogênio. Notou-se que a liga com cobalto apresentou a melhor capacidade de absorção de hidrogênio. Ademais, verificou-se o comportamento destas ligas na capacidade de descarga, estabilidade cíclica e na alta taxa de descarga de baterias de Ni-HM. A maior capacidade de descarga medida foi para a liga de cobalto, atingindo 337,1 mAh/g. Notou-se, posteriormente uma melhora na estabilidade cíclica das baterias com o aumento do teor de cobre. Além disso, observou-se que a alta taxa de descarga apresenta melhores valores com a adição de cobre na composição. Por fim, avaliou-se o efeito da susceptibilidade a corrosão. Notou-se que o estanho promove um aumento na resistência à corrosão das ligas em eletrólito alcalino.
Título en inglés
Influence of replacement of cobalt by tin and copper on microstructure and electrical properties of LaMgAlMnCoNi based alloys
Palabras clave en inglés
hydrogen storage alloys
LaNi5 based alloys
Ni-MH batteries
rare earths
Resumen en inglés
In this work, it has firstly been evaluated the effect of tin (Sn) and copper (Cu) substituting cobalt (Co) in LaMgAlMnCoNi AB5-type alloys for use in hydrogen storage materials and negative electrodes of Ni-MH batteries. The influence of this substitution on the microstructure of these materials has been evaluated. It could be noted that increasing the tin concentration promotes the formation of LaNiSn phase and decrease of two main phases of these alloys: LaNi5 and (La,Mg)Ni3. Additionally, the Rietveld refinement has been evaluated to quantify phases in each composition. Subsequently, it has been proposed a study of the hydrogen absorption in these alloys. It could be observed that the cobalt alloy showed the best hydrogen absorption capacity. Moreover, the behavior of these alloys has been investigated in the discharge capacity, cyclic stability and high rate dischargeability of Ni-MH batteries. The highest discharge capacity has been measured for cobalt alloy, reaching 337.1 mAh/g. It has been noted, further improvement in the cyclic stability batteries with increasing copper content in the alloys. Furthermore, it has been observed that the high rate dischargeability has better values with the addition of copper in the composition. Finally, it has been evaluated the effect of susceptibility to corrosion. It has been noted that tin promotes an increase in corrosion resistance of the alloys in an alkaline electrolyte.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-09-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.