• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.85.2017.tde-09082017-103559
Documento
Autor
Nombre completo
Rebeca da Silva Grecco Romano
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Lugão, Ademar Benévolo (Presidente)
Farah, Marcelo
Rosa, Derval dos Santos
Título en portugués
Estudo da irradiação do polipropileno para possibilitar o controle de sua degradação ambiental
Palabras clave en portugués
envelhecimento natural
irradiação gama
polipropileno
pró-degradante
Resumen en portugués
O PP é descartado em grande quantidade no meio ambiente, tendo em vista seu consumo muito elevado derivado de suas excelentes propriedades químicas e físicas, boa processabilidade e baixo custo. As radiações ionizantes, não ionizantes (UV e infravermelho), bem como o oxigênio e os poluentes podem causar a degradação do polipropileno (PP). A exposição à radiação ionizante pode causar na molécula de PP cisão de cadeia principal, reticulação e peroxidação (na presença de ar) entre outras. Este estudo tem como objetivo, o desenvolvimento de um PP oxidegradável por meio do controle da degradação induzida por radiação ionizante. As amostras foram processadas por injeção e expostas ao envelhecimento natural durante 180 dias e ao envelhecimento acelerado em estufa á 100°C por 192 dias e depois caracterizadas por avaliação visual, ensaios mecânicos, FTIR, SEM, DSC, TGA e DRX. As amostras de PP Grão 20 kGy, após o envelhecimento natural, apresentaram maior oxidação com presença de fissuras superficiais mais intensamente do que o PP d2w®. A resistência a tração do PP irradiado foi superior ao PP d2w® e os resultados do alongamento na ruptura mostraram uma diminuição intensa se compararmos o PP irradiado e o PP d2w® com o PP. Após a exposição natural espécies os índices de vinila e carbonila aumentaram ligeiramente devido as reações Norrish. O grupo carbonila promove uma oxidação contínua, junto à superfície fazendo com que o polímero diminua sua massa molar. O efeito da degradação natural foi evidente na ordem PP Grão 20 kGy > PP Grão 12,5 kGy = PP d2w® > PP. Por conseguinte, este conceito pode ser utilizado para produzir um PP com propriedades oxi-degradáveis de uma forma controlável.
Título en inglés
Study of polypropylene irradiation to ensure the control of its environmental degradation
Palabras clave en inglés
environmental aging
gamma irradiation
polypropylene
pro-degradant
Resumen en inglés
UV light, heat, and pollutants can interact with Polypropylene (PP) molecules, mainly with the tertiary carbon producing free radicals which can react with oxygen producing changes in its properties. PP has outstanding chemical and physical properties and a good processability at very low market price. In addition, PP is extensively used for manufacturing various kinds of products, however due to its large-scale consumption a lot of waste is generated at the end of their life cycle to the environment with low rate degradation. Controlled degradation of PP can be achieved by exposing the polymers to well defined parameters, such as absorbed dose, intemperies, oxygen, etc. In this study, structural changes in PP macro-molecule are created upon exposure to ionizing radiation such as: main chain scission, crosslinking and peroxidation (in presence of air). This study has the objective of comparing the environmental and accelerated exposures of PP neat, PP irradiated with 12,5 kGy and 20 kGy and the incorporation of the commercial pro-degradant d2w®. Dumbbell samples were manufactured by injection molding and exposed to the environment during 180 days and to accelerated aging to 192 days. The samples were characterized by Mechanical Testing, Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscopy (SEM), X-ray Diffraction (DRX) and Differential Scanning Calorimetry (DSC). The samples previously irradiated, PP 20 kGy, after environmental aging showed higher oxidation and presence of surface cracks than the PP d2w® and PP neat. They also showed presence of carbonyl groups, decreases in elongation at break, increase in Strength Modulus and decrease of melting temperature corroborating with degradation.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2017RomanoEstudo.pdf (2.36 Mbytes)
Fecha de Publicación
2017-08-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.