Dissertação de Mestrado
DOI
10.11606/D.85.2001.tde-07122005-141227
Documento
Autor
Nome completo
Renata Ayres Rocha
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2001
Orientador
Banca examinadora
Muccillo, Eliana Navarro dos Santos (Presidente)
Cosentino, Ivana Conte
Gouvea, Douglas
Título em português
Obtenção e Caracterização de Eletrólitos Sólidos de Céria-Gadolínia
Palavras-chave em português
caracterização
céria-gadolínia
eletrólitos sólidos
síntese
Resumo em português
Soluções sólidas de CeO2:Gd2O3 foram obtidas a partir de três técnicas de síntese que se utilizam de matrizes poliméricas: técnica dos precursores poliméricos ou citratos, técnica do citrato amorfo e técnica do PVA. O principal objetivo deste trabalho é a obtenção de pós reativos e cerâmicas sinterizadas densas. Para a caracterização dos materiais, foram analisadas as resinas precursoras, o pó calcinado a duas temperaturas e os compactos sinterizados. Os principais resultados mostram que: as soluções sólidas podem ser obtidas a temperaturas relativamente baixas; os pós apresentam tamanho nanométrico de partículas; a densificação é dependente da técnica de síntese e do teor de dopante. A técnica do PVA deve ser utilizada com cuidado, principalmente quando há possibilidade de ocorrer auto-ignição durante a decomposição térmica da resina precursora. Utilizando-se a técnica dos precursores poliméricos, o teor de carbono residual foi mais elevado do que nas outras duas técnicas, como esperado. A técnica do citrato amorfo foi a que permitiu obter cerâmicas mais densas. A resistividade elétrica da cerâmica sinterizada é função do teor de dopante, do teor de pureza e da porosidade, como sugerido na literatura.
Título em inglês
Preparation and Characterization of Ceria-Gadolinia Solid Electrolytes
Palavras-chave em inglês
ceria-gadolinia
characterization
solid electrolytes
synthesis
Resumo em inglês
CeO2:Gd2O3 solid solutions have been prepared by the following techniques based on polymeric matrices: the citrate, the amorphous citrate and the PVA techniques. The main purpose was to obtain reactive powders for preparing highly dense sintered ceramic pieces. The precursor resin, calcined powders and sintered compacts were studied by several techniques for complete characterization. The main results show that solid solutions may be obtained at relatively low temperatures and that powder particles are in the nanosize range, whatever is the technique used for the synthesis of the solid solution. However, the densification of sintered compacts is found to be dependent on dopant content and synthesis technique. The PVA technique should be used with caution, mainly due to combustion that may occur during precursor decomposition. The residual carbon content was found to be higher for powder prepared by the citrate technique. Specimens with high densification were obtained following the amorphous citrate technique. Electrical resistivity results are in agreement with previous results that suggest a dependence of the porosity of the sintered compacts on the dopant content and also on the material chosen for precursor.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2006-04-03
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.