Mémoire de Maîtrise
DOI
Document
Auteur
Nom complet
Odilon de Moraes Junior
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2019
Directeur
Jury
Pillis, Marina Fuser (Président)
Antunes, Renato Altobelli
Xavier, Marcos Domingos
Titre en portugais
Caracterização de um aço baixo carbono microligado ao vanádio utilizado na fabricação de componentes mecânicos
Mots-clés en portugais
aço microligado
aços HSLA
Charpy
resistência à tração
vanádio
Resumé en portugais
Os aços microligados representam, cada vez mais, uma parcela significativa de produção das usinas siderúrgicas para aplicações nos mais variados segmentos industriais tais como o automotivo, petróleo e gás, construção civil e agronegócio. A característica principal desses aços é a sua elevada resistência mecânica, aliada à boa tenacidade, ductilidade e soldabilidade; o que vem sendo obtido pela utilização de composições químicas específicas com teores baixos de carbono e de microligantes que conferem essas características a esses aços. Os microligantes utilizados são os mais variados, mas principalmente destaca-se a utilização do vanádio, nióbio, titânio, cobre, manganês, cromo, alumínio e nitrogênio. No presente trabalho foram estudadas as propriedades mecânicas de um aço microligado ao vanádio com 0,25%V e um aço AISI 1020. O aço microligado apresentou LRT, LE, alongamento e estricção de, respectivamente, 735,29 MPa, 559,07 MPa, 22,7% e 63,29%. O aço AISI 1020 apresentou, respectivamente, 437,42 MPa, 268,71MPa, 32,92% e 67,15%. O aço microligado apresentou propriedade mecânica superior à do aço AISI 1020 e ductilidade equivalente. Os resultados de impacto Charpy nas temperaturas de 23 °C, -20 °C e -40 °C foram, para o aço microligado, respectivamente de, 33,83 J, 12,41 J, e 6,54 J, e para aço AISI 1020 33,18 J, 5,07 J e 3,04 J, respectivamente. Observa-se tenacidade superior do aço microligado, quando comparado com o aço AISI 1020. O ensaio revelou microestruturas refinadas em ambos os aços, e tamanho de grão de 18μm n° 8 ASTM E 112 e de 25 μm n° 7 para o aço microligado e para o AISI 1020, respectivamente. Os testes eletroquímicos realizados em uma solução aquosa 3,5% em peso de NaCl revelaram que o aço microligado apresentou formação de camada passiva, e mostrou-se menos resistente à corrosão.
Titre en anglais
Characterization of a low carbon vanadium microalloyed steel used in the manufacture of mechanical components
Mots-clés en anglais
Charpy
HSLA steels
microalloyed steel
tensile strength
vanadium
Resumé en anglais
Microalloyed steels are representing significant portion and increasingly steelmakers production and they are being applied to several industrial market segments such as automotive, oil and gas, civil construction and agribusiness. Its main characteristics are the superior tensile strength, toughness, ductility and good weldability. These properties are obtained through specific chemical compositions as low carbon and microalloying elements contents. Several microalloying elements can be used but some of them need to be mentioned such as vanadium, niobium, titanium, cooper, manganese, chromium, aluminum and nitrogen. In this work, the mechanical properties of a vanadium microalloyed and AISI 1020 steels were studied and compared. The microalloyed steel presented LRT, LE, elongation and toughness values of, respectively, 735.29 MPa, 559.07 MPa, 22.7% and 63,29%. AISI 1020 presented, respectively, 437.41 MPa, 268.70 MPa, 32.92% and 67.15%. The microalloyed steel presented mechanical properties superior to AISI 1020 and equivalent ductility. The results of the Charpy impact tests at the temperatures of 23 ° C, -20 ° C and -40 ° C were 33.83 J, 12.41 J, 6.54 J for the microalloyed steel, and for AISI 1020 steel the values were 33,18 J, 5.07 J and 3.04 J, respectively. The superior toughness of the microalloyed steel is observed when compared to the AISI 1020 steel. The metallographic examination showed fine grain microstructures ASTM E 112 No.8 and 7.for the microalloyed and for the AISI 1020, respectively. The electrochemical tests carried out in a 3.5 wt% NaCl aqueous solution showed that the microalloyed steel is less resistant to corrosion, and that a passive layer was formed on its surface.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2019-06-13
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.