Disertación de Maestría
DOI
10.11606/D.85.2014.tde-05122014-083916
Documento
Autor
Nombre completo
Luiz Antônio Rossi Jazbinsek
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2014
Director
Tribunal
Costa, Isolda (Presidente)
Ramanathan, Lalgudi Venkataraman
Rodrigues, Paulo Rogerio Pinto
Título en portugués
Investigação de tratamentos alternativos de fosfatização para eliminação do níquel e cromo hexavalente
Palabras clave en portugués
corrosão
cromo
fosfato
nióbio
níquel
Resumen en portugués
O processo de fosfatização é amplamente utilizado na indústria de tratamento de superfície de metais, especialmente de placas de baixa espessura, melhorando a aderência entre a superfície do metal e o revestimento de tinta, e aumentando a durabilidade dos sistemas de pintura contra ataques corrosivos. Os fosfatos tricatiônicos contendo zinco, níquel e manganês são comumente aplicados em aço, e muito se discute sobre a substituição do níquel por outro elemento com o objetivo de obter um fosfato mais amigável ao meio ambiente, tanto em seus processos como para as pessoas envolvidas. O nióbio tem sido avaliado nesse sentido. Os impactos ambientais mais significativos dos fosfatos estão relacionados com a presença do níquel e do cromo hexavalente utilizado no processo, devido a exposição ao contato humano e a contaminação residual da água e do solo. Seguindo a linha de pesquisa que estudou a substituição do níquel por nióbio em camadas formadas sobre o aço carbono, o presente estudo avaliou e caracterizou camadas de fosfato contendo zinco, manganês e nióbio, formadas em aço galvanizado, comparando os resultados com o fosfato de zinco, manganês e níquel, bem como com o fosfato de zinco e manganês, sem a adição de nióbio. Embora o uso de cromo não seja recomendado mundialmente, ainda hoje é utilizado no processo de selagem da porosidade da camada de fosfato, em banhos contendo cromo hexavalente, que é reconhecido por ser carcinogênico, estando associado a várias doenças. Devido às características passivantes do nióbio, este estudo também avaliou o banho tricatiônico contendo oxalato amoniacal de nióbio, como etapa de passivação das camadas, tanto em banhos bicatiônicos, quanto nos tricatiônicos, com resultados muito interessantes como opção de substituição do cromo hexavalente. Os resultados obtidos neste trabalho são promissores, pois algumas das formulações contendo nióbio se apresentaram equivalentes ao fosfato contendo níquel, tanto em morfologia, verificadas em microscopia eletrônica de varredura, ensaios gravimétricos, de porosidade e de aderência, quanto nas características de proteção anticorrosivas, verificadas nos ensaios eletroquímicos e em câmara de névoa salina. Embora apresentando eficácia compatível com fosfato contendo níquel, ajustes na estabilidade dos banhos ainda são necessários e mais estudos utilizando técnicas voltadas para o entendimento dos fenômenos que ocorrem na base dos poros, devem orientar as próximas etapas da linha de pesquisa.
Título en inglés
Investigation of alternative phosphating treatments for nickel and hexavalent chromium elimination
Palabras clave en inglés
chromium
corrosion
nickel
niobium
phosphate
Resumen en inglés
The phosphating processes are widely used in industry as surface treatments for metals, especially for low thickness plates, improving the adhesion between the metallic surface and the paint coating, and increasing the durability of paint systems against corrosion attacks. The tricationic phosphates containing zinc, nickel and manganese are commonly applied on steel. There is much discussion about the replacement of nickel by another element in order to have an environmentally friendly phosphating process. Niobium as a replacement for nickel has been evaluated. The most significant environmental impacts of phosphating processes are related to the presence of nickel and hexavalent chromium used in the process, this last as a passivation treatment. Nickel and hexavalent chromium are harmful to human and environment leading to contamination of water and soil. In the present study phosphate layers containing zinc, manganese and niobium have been evaluated and characterized on galvanized steel, and the results were compared with phosphates containing zinc, manganese and nickel, or a bicationic phosphate layer with zinc and manganese. Although the use of hexavalent chromium is not recommended worldwide, it is still used in processes for sealing the porosity of phosphate layers. This element is carcinogenic and has been associated with various diseases. Due to the passivation characteristics of niobium, this study also evaluated the tricationic bath containing niobium ammonium oxalate as a passivation treatment. The results showed that it could act as a replacement for the hexavalent chromium. The results of the present study showed that formulations containing niobium are potential replacements for hexavalent chromium and similar corrosion protection was obtained for the phosphate containing nickel or that with niobium. The morphology observed by scanning electron microscopy, gravimetric tests, porosity and adhesion evaluation results indicated that the phosphate obtained with passivation treatment in niobium containing solution could be considered as a promising alternative to replace passivation with hexavalent chromium ions. Despite of the promising results, adjustments in the baths to obtain stability are still needed and should guide the next steps of the subject of this research.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-12-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.