Doctoral Thesis
DOI
10.11606/T.85.2013.tde-04072013-172258
Document
Author
Full name
Carola Gomez Agreda
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Bressiani, Ana Helena de Almeida (President)
Queiroz, Alvaro Antonio Alencar de
Rigo, Eliana Cristina da Silva
Yoshimoto, Marcelo
Zavaglia, Cecília Amélia de Carvalho
Title in Portuguese
Ticp e liga Ti-13Nb-13Zr com diferentes tratamentos de superfície-testes in vitro e in vivo
Keywords in Portuguese
metalurgia do pó
osteointegração
teste \"in vitro\"
teste \"in vivo\"
tratamentos de superfície
Abstract in Portuguese
O titânio e suas ligas são biomateriais metálicos extensamente utilizados em aplicações médicas e odontológicas, apesar de não formarem ligação química com o osso circundante. Por isto é desejável técnicas que proporcionem a bioatividade na superfície desses metais. A proposta deste estudo foi avaliar e comparar, por testes in vitro e in vivo o comportamento de Ticp e da liga Ti-13Nb-13Zr utilizando diferentes tratamentos de superfície frente à formação do recobrimento biomimético e ao processo de osteointegração. Foram utilizadas placas comerciais de Ti e amostras da liga e de Ticp, obtidas por M/P. As amostras foram submetidas a quatro diferentes tratamentos de superfície (padrão - tratamento alcalino; 1°- tratamento alcalino e térmico; 2°- tratamento ácido e alcalino; 3º- tratamento alcalino, CaCl2, térmico e água quente), analisadas quanto à formação de apatita em SBF em períodos de 1 a 21 dias. Os recobrimentos obtidos foram caracterizado por MEV e DRIFT. Para a avaliação in vivo dos implantes, obtidos por M/P, de Ticp e da liga, com e sem tratamentos superficiais, foram utilizados coelhos adultos machos. A avaliação teve duração de 7 semanas em que foram aplicados marcadores celulares ósseos em tempos e sequência específicos do pós-operatório. Na avaliação in vitro, os recobrimentos de maior espessura foram nas amostras obtidas por M/P, comparativamente à amostra laminada. Todos os tratamentos foram efetivos na promoção da bioatividade. O 2º tratamento obteve recobrimento com maior espessura nos períodos avaliados para todas as superfícies. Na avaliação in vivo, ocorreu crescimento ósseo com osteointegração em todos os implantes com e sem tratamentos superficiais. O crescimento ósseo na interface osso/implante ocorreu de forma contínua em todo o período de reparação para o Ticp, o Ticp com tratamento padrão, o Ticp com o 2º tratamento e a liga com o 1° tratamento; e ocorreu de forma mais intensa no primeiro e terceiro período de reparação para os demais implantes. Os resultados dos testes in vitro e in vivo não são passíveis de analogia direta neste estudo, pois forneceram informações importantes sobre a formação, morfologia e taxa de aposição do recobrimento aos diferentes tratamentos de superfície e a efetividade da osteointegração destes tratamentos de superfície em modelo animal.
Title in English
Ticp and Ti-13Nb-13Zr alloy with different surface treatments in vitro and in vivo tests
Keywords in English
osseointegration
powder metallurgy
surface treatments
\"in vitro\" test
\"in vivo\" test
Abstract in English
Titanium and its alloys are widely used metallic biomaterials in medical and dental applications for patient rehabilitation. However, these materials cannot bond with surrounding bone. For this reason, it is desirable to provide a bone-bonding ability for metallic surface. The aim of this study was to evaluate and compare in vitro and in vivo tests of Ti and Ti-13Nb-13Zr alloy subjected to different surface treatments. Laminate titanium plates and Ti and alloy Ti samples obtained by powder metallurgy were used in this study. The samples were subjected to four different surface treatments (pattern- alkali treatment; 1°- alkali and heat treatments; 2°- acid and alkali treatments; 3°- alkali, CaCl2,heat and hot water treatments) and evaluated for apatite coating in SBF for periods of 1 to 21 days. The coated specimens were analyzed by SEM (surface and cross section) and DRIFT. For in vivo evaluation of osseointegration were used Ticp and alloy implants obtained by powder metallurgy with and without surface treatments in male adult rabbits. The evaluation was 7 weeks which were applied bone cell markers at selected times. In vitro evaluation, surfaces obtained by powder metallurgy had a coating of greater thickness when compared to the laminate surface. All treatments were effective in promoting the bioactivity. The 2nd treatment provided coating thicker in the evaluation periods for all surfaces. The osseointegration occurred in all implants with and without surface treatments. However, growth in the bone/ implant interface was continued all over repair period for Ticp, Ticp with pattern treatment, Ticp with 2nd treatment and alloy with 1st treatment. Bone growth in interface occurred more intensely for first and third period to repair for remaining implants. In vitro and in vivo tests are not liable to direct analogy in this study because provided important information on the formation, morphology and apposition rate of coating on different surface treatments and the effectiveness of osseointegration in animal model.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
2013AgredaTicp.pdf (12.98 Mbytes)
Publishing Date
2013-07-30
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.