• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.85.2008.tde-03092009-145609
Documento
Autor
Nombre completo
Wander Burielo de Souza
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Parra, Duclerc Fernandes (Presidente)
Otaguro, Harumi
Wiebeck, Helio
Título en portugués
Estudo da adição de lama de bauxita em polímero de poli(metacrilato de metila) por meio de polimerização em massa e moldagem em casting
Palabras clave en portugués
Compósito
lama de bauxita
poli (metacrilato de metila)
Resumen en portugués
O trabalho refere-se ao desenvolvimento de formulações de poli (metacrilato de metila) (PMMA) contendo lama de bauxita proveniente de processo Bayer. A adesão entre a lama de bauxita e o poli (metacrilato de metila) ocorreu em todas as concentrações testadas (10-70%), mostrando o aumento progressivo das propriedades mecânicas de resistência à tração, resistência à flexão e módulo de elasticidade na tração como na flexão. As propriedades mecânicas são compatíveis com as diversas finalidades de emprego de superfícies sólidas. A estabilidade térmica do composto de poli (metacrilato de metila) com alto nível de lama de bauxita (70%) é semelhante a do material padrão estudado. Os estudos de citoxidade revelam que superfícies sólidas obtidas a partir de lama vermelha não possuem toxidade nas condições testadas.
Título en inglés
STUDY OF RED MUD ADDITION IN THE POLI (METHYL METACRYLATE) BY MASS POLIMERIZATION AND CASTING PROCESS MOLDING
Palabras clave en inglés
Compósito
lama de bauxita
poli (metacrilato de metila)
Resumen en inglés
The work refers to the development of formulations of poly (methyl metacrylate) (PMMA) and red mud from Bayer process. The adhesion between PMMA and the filler was achieved in the experimental concentration range (10-70%), showing progressive increase of mechanical properties as flexion resistance and modulus. Other mechanical properties are compatible with service life of solid surfaces. The results of thermal stability indicated that formulation with red mud high content (70%) are similar to the standart. Citotoxicity tests revealed no toxicity of the materials in the test conditions.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-09-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.