• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Master's Dissertation
DOI
https://doi.org/10.11606/D.85.2012.tde-24082012-135026
Document
Author
Full name
Daniel de Abreu Rossetto
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2012
Supervisor
Committee
Saxena, Rajendra Narain (President)
Carbonari, Artur Wilson
Cavalcante, Fabio Henrique de Moraes
Title in Portuguese
Investigação de interações hiperfinas em pó e filmes finos de dióxido de háfnio  pela técnica de correlação  angular gama-gama perturbada
Keywords in Portuguese
correlação angular perturbada
dielétricos
dióxido de Háfnio
física
interação hiperfina
Abstract in Portuguese
Neste trabalho foi realizada a investigação de interações hiperfinas em amostra nano estruturadas e filmes finos de dióxido de háfnio por meio da técnica de correlação angular gama-gama perturbada (CAP), com o intuito de realizar um estudo sistemático do comportamento dos parâmetros quadrupolares com a temperatura de tratamento térmico. Para a realização destas medidas foi utilizada a ponta de prova 181Hf -> 181Ta que foi produzida na própria amostra por irradiação, no reator IEA-R1 do IPEN. As amostras foram obtidas através do processo químico sol-gel e as análises dos compostos realizadas por difração de raios-X, EDS e MEV. As amostras em forma de pó foram todas produzidas pelo Laboratório de Interações Hiperfinas do IPEN, no entanto o filme fino com espessura de 10nm foi produzido pelo Centro de Lasers e Aplicações (CLA) do IPEN e o filme fino de espessura de 409nm foi produzido pelo Laboratório de Interações Hiperfinas da Universidade de Lisboa. As medidas foram realizadas todas à temperatura ambiente e os resultados mostraram que a fase monoclínica encontra-se presente em todas as amostras e sua fração tende a aumentar sempre com o aumento da temperatura de tratamento térmico na qual foram submetidas às amostras. A impurificação de algumas amostras com elementos Co e Fe foi realizada com a intenção de se observar o comportamento da amostra em função da temperatura de tratamento térmico e também verificar a existência de ferromagnetismo à temperatura ambiente.
Title in English
Hyperfine Interaction study in the powder and thin films of HfO2 by Perturbed Angular Correlation Technique
Keywords in English
Hafnium dioxide
Hyperfine Interaction
Perturbed Angular Correlation
Physics
Abstract in English
Hyperfine interactions in the powder samples and nanostructured thin films of hafnium dioxide have been studied through the perturbed angular correlation (PAC) technique in order to perform a systematic study of the behavior of quadrupole parameters with the annealing temperature. The PAC measurements were performed with the 181Hf -> 181Ta probe. The probe was produced by the neutron irradiation in the IEA-R1 nuclear reactor of IPEN. Samples were prepared using sol-gel chemical process. The samples were analyzed by X-ray diffraction, SEM and EDS. The powder samples were all produced in the Laboratory of Hyperfine Interactions of IPEN, however the thin film with a thickness of 10nm was produced by the Lasers and Applications Center (CLA) of IPEN and the thin film of a thickness of 409nm were produced by the Hyperfine Interactions Laboratory of the Lisbon University. All the measurements were perform at room temperature and showed that the monoclinic phase is present in all the samples and their fraction tends to increase with increasing annealing temperature to which the samples were submitted. Some of the samples were doped with 3d elements Co and Fe in order to observe the possible existence of ferromagnetism at room temperature.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2012-11-09
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.