Disertación de Maestría
DOI
10.11606/D.85.2018.tde-23042018-093927
Documento
Autor
Nombre completo
Ana Paula Funari
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Mathor, Monica Beatriz (Presidente)
Guimarães, Rodrigo Pereira
Moura, Rafael Traldi
Título en portugués
Avaliação morfológica e biomecânica de tecido tendinoso humano esterilizado por radiação ionizante
Palabras clave en portugués
banco de tecido
esterilização
radiação ionizante
tendão
Resumen en portugués
O crescente aumento do interesse no desenvolvimento em técnicas cirúrgicas menos invasivas, como nas reconstruções tendíneas e ligamentares, tem levado ao aumento das pesquisas referentes ao uso de aloenxertos esterilizados por radiação ionizante. O processamento por radiação ionizante é um método seguro e não deixa resíduos, sendo utilizado como esterilização final. O presente estudo teve como proposta avaliar os efeitos da aplicação de radiação ionizante, produzida por fonte de 60Co, em amostras de tendões humanos pré processados de doadores multiorgãos obtidas por meio de colaboração com Bancos de Tecidos. O pré-processamento das amostras deu-se por métodos químicos e preservação por congelamento em -80 °C. As doses aplicadas no processamento por radiação foram de 12,5 kGy, 15,0 kGy e 25,0 kGy, cada uma com seu respectivo controle não irradiado. As amostras foram avaliadas por meio de testes histológicos, ópticos e biomecânicos, com o objetivo de analisar possíveis modificações morfológicas e estruturais. Os resultados apresentados demonstraram que o processamento por ultrassom e peróxido de hidrogênio causaram alterações na morfologia dos tecidos, o que ocasionou danos à sua estrutura, inviabilizando as amostras. Nas amostras processadas por álcool e antibiótico não foram observados danos na rede de colágeno pela aplicação da radiação. Os resultados dos testes biomecânicos apresentaram diferenças significativas entre os métodos aplicados. As amostras processadas com álcool e antibiótico apresentaram perda pouco significativa no módulo de elasticidade, comparadas às amostras processadas por ultrassom e peróxido de hidrogênio que mantiveram a propriedade viscoelástica. Contudo na dose de 12,5 kGy foi observado um aumento no módulo elástico e na viscoelasticidade. Com base nas análises, podemos concluir que o método de processamento com álcool, antibiótico e irradiação demonstrou menor dano, tanto na biomecânica quanto na esterilização, sendo que as amostras irradiadas a 15,0 e 25,0 kGy apresentaram características semelhantes ao controle não irradiado.
Título en inglés
Morphological and biomechanical evaluation of human tendon tissue sterilized by ionizing radiation
Palabras clave en inglés
ionizing radiation
sterilization
tendon
tissue bank
Resumen en inglés
The increasing interest of development in less invasive surgical techniques, such as reconstructions of ligament tendon, has led to the increase of the research concerning the use of Allografts sterilized by ionizing radiation. Processing by ionizing radiation is a safe method and leaves no residues, being used as final sterilization. The present study was to evaluate the effects of proposed application of ionizing radiation, produced by 60Co source in human tendon pre-samples processed multiorgans donors obtained through collaboration with tissue banks. The pre-processing of samples given by chemical methods and preserved by freezing at -80 °C. The doses applied in radiation processing were 12.5, 15.0 and 25.0 kGy, each with your corresponding non-irradiated control. The samples were evaluated by means of histological and biomechanical testing, with the purpose of analyzing possible structural and morphological changes. The results showed that the ultrasound processing and hydrogen peroxide caused changes in the morphology of the tissues, which caused damage to the structure, making your samples. In the samples processed by alcohol and antibiotics were not observed damage on the network of collagen by the application of radiation. The results of biomechanical tests showed significant differences between the methods used. The samples processed with alcohol and antibiotics showed negligible loss in modulus of elasticity compared with the samples processed by ultrasound and hydrogen peroxide which kept the viscoelastic property, however in 12.5 kGy dose was observed an increase in elastic modulus and viscoelasticity. Based on the analysis we can conclude that the method of processing with alcohol, antibiotics and irradiation showed less damage, both in biomechanics and sterilization, in the samples irradiated with 15.0 and 25.0 kGy, showing results similar to the non-irradiated control.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-05-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.