Tese de Doutorado
DOI
https://doi.org/10.11606/T.76.2014.tde-21102014-093430
Documento
Autor
Nome completo
Ivan Braga Gallo
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2014
Orientador
Banca examinadora
Zanatta, Antonio Ricardo (Presidente)
Catunda, Tomaz
Iikawa, Fernando
Li, Maximo Siu
Silva, José Humberto Dias da
Título em português
Microcavidades ópticas à base de silício: projeto, confecção e propriedades
Palavras-chave em português
Coeficiente termo-óptico
Fotoluminescência no infravermelho
Microcavidades ópticas
Silício amorfo
Terras-raras
Resumo em português
Estruturas fotônicas à base de silício têm despertado grande interesse por permitirem uma perfeita integração entre processos ópticos e eletrônicos em um único chip. Além de compatíveis com a atual indústria microeletrônica, acredita-se, que tais estruturas possam aumentar consideravelmente a velocidade de processamento de informações. Uma microcavidade óptica é um exemplo de estrutura fotônica simples. Feita à base de silício, e dopada com íons terra-rara, tal microcavidade pode intensificar a emissão gerada pelo íon e resultar em um dispositivo de importância tecnológica. O projeto-construção deste tipo de microcavidade deve considerar a sua região de funcionamento e os materiais a serem utilizados. Deve contemplar, ainda, algumas condições externas que, eventualmente, possam alterar o seu funcionamento. Uma dessas condições é descrita pelo chamado coeficiente termo-óptico que indica a dependência do índice de refração com a temperatura. Dentro desse contexto a presente Tese de Doutorado foi dedicada ao estudo de microcavidades ópticas com janelas de transmissão em 650 nm e em 1550 nm – correspondendo às regiões de menores perdas de fibras ópticas de plástico e de sílica. As microcavidades compreenderam espelhos de Bragg [camadas alternadas de silício amorfo (a-Si) e nitreto de silício amorfo (a-SiN)], um filme de a-SiN como espaçador, e foram depositadas sobre substratos de sílica pela técnica de sputtering. As cavidades MC-Er e MC-ErYb tiveram como espaçadores filmes de a-SiN dopados com Er e Er + Yb, respectivamente. Medidas de fotoluminescência da MC-ErYb na região do infravermelho próximo indicaram um aumento de 48 vezes na emissão dos íons Er3+ (em ~1535 nm) comparado a um filme de a-SiN dopado com érbio devido: (1) a presença do itérbio e, (2) às múltiplas reflexões sofridas pela luz nos espelhos de Bragg. As microcavidades cujos espaçadores eram a-SiN puro foram submetidas a medidas de transmissão óptica em função da temperatura de medida. O deslocamento da janela de transmissão devido às variações de temperatura permitiu determinar o valor do TOC do a-SiN como: (6.2±0.1)×10-5 ºC-1 (em ~ 620 nm) e, (4.7±0.1)×10-5 ºC -1 (em ~ 1510 nm). Até onde sabemos, o TOC do a-SiN no VIS foi determinado pela primeira vez neste trabalho.
Título em inglês
Silicon based optical microcavities: project, construction and properties
Palavras-chave em inglês
Amorphous silicon
Near infrared photoluminescence
Optical microcavities
Rare-earths
Thermo-optic coefficient
Resumo em inglês
Silicon photonic based structures have attracted great interest for allowing a perfect integration between optical and electronic process in a single chip. Besides being compatible with the actual microelectronic industry, it is believed that such structures can considerably increase the information processing speed. An optical microcavity is an example of a simple photonic structure. Made based on silicon, and doped with rare-earth ions, such microcavity may enhance the emission generated by the ion and become a device of technological importance. The project-construction of this kind of microcavity has to consider the operation region and the materials used. It still has to take into account external conditions that may, eventually, change its operation. One of these conditions is described by the thermo-optic coefficient (TOC) that shows the dependence of the refractive index with the temperature. Within this context the present PhD thesis was dedicated to the study of optical microcavities with transmission windows at 650 nm and at 1550 nm – corresponding to the low losses regions of the plastic and silica optical fibers. The microcavities comprised Bragg mirrors [alternated layers of amorphous silicon (a-Si) and amorphous silicon nitride (a-SiN)], one film of a-SiN as spacer, and were deposited on silica substrates by the sputtering technique. The MC-Er and MC-ErYb cavities had Er and Er+Yb-doped a-SiN films as spacers, respectively. Photoluminescence measurements of the MC-ErYb in the near infrared showed an enhancement of 48 times in the emission of the Er3+ ions (at ~ 1535 nm) compared with an Er-doped a-SiN film owing to: (1) the presence of ytterbium and, (2) the multiple reflections experienced by the light at the Bragg mirrors. The microcavities whose spacers were pure a-SiN were submitted to optical transmission measurements as a function of the measurement temperature. The shift of the transmission window due to variations in the temperature allowed determining the a-SiN TOC: (6.2±0.1)×10-5 ºC-1 (at ~ 620 nm) and, (4.7±0.1)×10-5 ºC -1 (at ~ 1510 nm). To the best of our knowledge, the a-SiN TOC in the visible was determined for the first time in this work.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2014-10-30
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • GALLO, I. B., and Zanatta, A. R. A simple-versatile approach to achieve all-Si-based optical micro-cavities [doi:10.1063/1.4793592]. Journal of Applied Physics [online], 2013, vol. 113, p. 083106.
  • GALLO, I. B., BRAUD, A., and Zanatta, A. R. Efficient 1535 nm light emission from an all-Si-based optical micro-cavity containing Er^3+ and Yb^3+ ions [doi:10.1364/oe.21.028394]. Optics Express [online], 2013, vol. 21, p. 28394.
  • Zanatta, Antonio R., and GALLO, IVAN B. The Thermo Optic Coefficient of Amorphous SiN Films in the Near-Infrared and Visible Regions and Its Experimental Determination [doi:10.7567/apex.6.042402]. APPL PHYS EXPRESS [online], 2013, vol. 6, p. 042402.
  • Gallo, IB, and Zanatta, A. R. Influence of the temperature and time of thermal annealing in the optical properties of a-SiN. In Encontro Nacional de Física da Matéria Condensada, Foz do Iguaçu, 2011. Caderno de Resumos.SP : Sociedade Brasileira de Física, 2011. Abstract.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2024. Todos os direitos reservados.