Disertación de Maestría
DOI
https://doi.org/10.11606/D.76.2012.tde-14062012-081041
Documento
Autor
Nombre completo
Wesley de Souza Bezerra
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2012
Director
Tribunal
Azevêdo, Eduardo Ribeiro de (Presidente)
Atvars, Teresa Dib Zambon
Venâncio, Tiago
Título en portugués
Dinâmica molecular e formação de domínios em copolímeros em bloco estudados por RMN de alta e baixa resolução
Palabras clave en portugués
Copolímeros em bloco
Difusão de Spins
PMAPEG
POE
RMN
Resumen en portugués
O objetivo desta dissertação é a utilização de metodologias de RMN para caracterizar a separação de fases e, em algum grau, a dinâmica de segmentos moleculares em copolímeros em bloco. Na primeira parte do trabalho, técnicas de RMN de Difusão de Spins, cujo fenômeno envolvido traz informações sobre a formação de domínios de segmentos moleculares, foram exploradas no sentido de avaliar seu desempenho assim como as principais dificuldades experimentais. Para isso, foi usado como referência o copolímero tri-bloco SEBS (Estireno-EtilenoButileno-Estireno), cuja morfologia é bem conhecida. Os testes experimentais foram realizados em equipamentos de RMN com campo magnético de 0.5 T e 9.4 T, sendo que em baixo campo uma proposta alternativa de tratamento dos dados foi utilizada. Como já apontado na literatura, os resultados indicaram que embora seja possível realizar tais experimentos em baixo campo a análise dos dados se torna mais complexa devido aos tempos de relaxação T1 mais curtos, tornando necessário o uso de simulações numéricas, que fazem a análise mais dependente de modelos específicos. A segunda parte do trabalho foi dedicada ao estudo de copolímeros em bloco compostos por polióxidoetileno (POE) ou Polietileno Glicol (PEG - POE de baixo peso molecular) e poliestireno (PS) e atambém copolimeros a base de PS e acrilatos ramificados com POE (PMAPEG - do inglês Poly Methyl Acrilate Polyethylene Glicol). Nesses estudos, técnicas de RMN de 1H e 13C como função da temperatura foram usadas para estudar as principais transições dinâmicas das cadeias de POE. Foi demonstrado que, embora o comportamento dinâmico das cadeias de POE seja similar em todos os copolímeros estudados, nas amostras de copolímeros com PMAPEG o grau de heterogeneidade dos movimentos das cadeias de POE é consideravelmente menor, o que foi atribuído ao empacotamento local semelhante e mais regular nos segmentos PMAPEG. Experimentos de RMN de Difusão de Spins foram utilizados nos estudos de morfologia, sendo demonstrada a separação de fases com formação de domínios em todas as amostras, com a regularidade desses domínios dependendo da composição. As dimensões médias dos domínios foram estimadas e os resultados correlacionados com os aspectos dinâmicos.
Título en inglés
Molecular dynamics and formation of domains in block copolymers studied by high and low resolution NMR
Palabras clave en inglés
Block Copolymers
NMR
PMAPEG
POE
Spin Diffusion
Resumen en inglés
The main objective of this dissertation is the use of NMR methods to characterize the phase separation and, to some extent, the dynamics of the molecular segments in block copolymers. In the first part, NMR Spin Diffusion methods were explored in order to evaluate their performance as well as the main experimental difficulties. For that, a reference tri-block polymer SEBS (styrene-block-butadiene-block-styrene), which had a well known morphology, was used. The experimental tests were carried out in NMR equipments with magnetic field of 0.47 T and 9.4 T and at low filed an alternative proposal for data analysis was used. A already shown in the literature, the results indicated that , despite being possible to accomplish these experiments in low field, the data analysis become more intricate due to the shorter T1 values at this magnetic field, requiring the use of numerical simulations, which make the method more model dependent. The second part was dedicated to the study of copolymers consisting of Polyoxyethylene (PEO) or Polyethylene Glycol (PEG-low molecular weight PEO) and polystyrene (PS) as well as copolymers based on PS and Poly acrylates with PEO branches (PMAPEG -Poly Methyl Acrylate Polyethylene Glicol). In these studies, 1H and 13C NMR methods as function of temperature were used to characterize the main dynamic transitions in the PEO chains. It was shown that, despite similar dynamic behavior was observed in all samples, the PS-PMAPEG copolymers present a smaller degree of motional heterogeneity, which was attributed to the similar local packing of the PMAPEG chains. Using Spin diffusion NMR information about the morphology of the samples were obtained, showing evidences of phase separation and domain formation in all samples, being the regularity of the domain related with the sample composition. The average domain sizes were estimated.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-06-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.