Tesis Doctoral
DOI
https://doi.org/10.11606/T.76.1997.tde-12112007-161134
Documento
Autor
Nombre completo
Marta Bueno de Moraes
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1997
Director
Tribunal
Bretas, Rosario Elida Suman (Presidente)
Bulhões, Luiz Otávio de Sousa
Frollini, Elisabete
Oliveira Junior, Osvaldo Novais de
Paoli, Marco Aurelio de
Título en portugués
Propriedades elétricas e físico-químicos de blendas de poli (sulfeto de p-fenileno) - pps com um cristal líquido polimérico (LCP)
Palabras clave en portugués
Cristal líquido polimerico
Polímeros
Polímeros condutores
Resumen en portugués
O poli (sulfeto de p-fenileno) - (PPS) é um termoplástico de engenharia de elevada resistência térmica e química com uma crescente importância industrial. já que pode ser utilizado na fabricação de filamentos, filmes e moldados por injeção. Este polímero tem mostrado grande habilidade de ser dopado para a produção de um material eletricamente condutivo (σ = 10 S/cm, na dopagem com AsF5), porém sua estrutura morfológica é bastante destruída quando dopado com estes fortes agentes oxidantes. Neste trabalho. o PPS foi dopado com agentes dopantes mais fracos como o tetracianoquinodimetano (TCNQ), para que não ocorresse a destruição da morfologia e assim, a sua influência pudesse ser melhor estudada. Diversas morfologias de PPS com TCNQ foram produzidas variando as condições de processamento. Foi analisado o efeito da adição de um segundo polímero, um cristal líquido termotrópico (TLCP), nas características microscópicas e na orientação do PPS e, conseqüentemente, no efeito destes parâmetros sobre a condutividade final das misturas destes dois polímeros. Foi verificado um efeito negativo do TLCP sobre a condutividade do PPS, já que o primeiro teve sua condutividade diminuída com a dopagem. Além disso, o LCP só induziu orientação no PPS a concentrações acima de 80% de TLCP na blenda. Verificou-se para o PPS que não é a orientação, mas sim a cristalinidade, o fator importante na sua condutividade final. O mecanismo de condução apresentado pelo PPS e blendas tanto puro quanto dopados com TCNQ, é o de salto de portadores entre níveis de impurezas (''hopping").
Título en inglés
Electrical and physical chemistry properties of poli (p-phenylene sulfide) with a liquid crystal polymer
Palabras clave en inglés
Concuctors polymers
Liquid crystal polymeric
Resumen en inglés
Poly (p-phenylene sulphide) (PPS) is an engineering thermoplastic, with high thermal and chemical resistance, and. with a growing industrial importance, due to its easy processability in the form of films, fiaments and injection molded articles. It also can be chemically doped and. therefore be a conductive polymer (σ = 10 S/cm, by doping with AsF5); however, when doping with strong oxidative agents, its morphology is destroyed. In this work, PPS was doped with a weaker doping agent, tetracyanoquinodimethane (TCNQ) in order to preserve its initial morphology and to study its influence on the final conductivity values. Different PPS/TCNQ morphologies were produced by varying the processing conditions. It was also studied the influence the blending of PPS/TCNQ with a liquid crystalline polymer (LCP) has on the microstructure and orientation of the PPS and on its conductivity. It was observed that this addition has a negative effect on the PPS conductivity. Orientation of the PPS by the LCP was only achieved at 80% wt LCP. It was concluded that, for the PPS, the major influence on its electrical conductivity is given by its amount of crystallinity, not by its orientation. The conduction mechanism of the PPS and its blends with the LCP doped with TCNQ is a hopping mechanism.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MartaMoraes.pdf (9.09 Mbytes)
Fecha de Publicación
2007-11-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.