Dissertação de Mestrado
DOI
10.11606/D.76.1994.tde-09042008-084147
Documento
Autor
Nome completo
Ricardo Costa de Santana
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1994
Orientador
Banca examinadora
Terrile, Maria Cristina (Presidente)
Magon, Claudio Jose
Mastelaro, Valmor Roberto
Título em português
RPE do ion Fe3+ em monocristais e fibras de LiNbO3
Palavras-chave em português
Campo cristalino
Impurezas magnéticas
RPE
Resumo em português
O objetivo deste trabalho foi o estudo do íon Fe3+ em monocristais e fibras monocristalinas de LiNbO3, através da técnica espectroscópica da Ressonância Paramagnética Eletrônica (RPE), nas freqüências de 10 e 34GHz, à temperatura ambiente. O Hamiltoniano de Spin para o íon Fe3+ ocupando um sítio de simetria trigonal (C3v) é dado por: H = 'beta' 'VET.H' 'VET.g' 'VET.S' + 'B20O20+B40O40 . Foram analisadas três amostras de LiNbO3, com diferentes concentrações de Fe3+ e os parâmetros de campo cristalino e fator-g encontrados são: fibra (0.3 mol% de Fe3+) g = 1.9908 '+OU-' 0.0002, 'B. SUP. 0 INF. 2' = 5.4'+OU-'0.2x10-2 cm-1 , 'B. SUP. 0 INF. 4' = -7.7'+OU-'1.5x10-5cm-1, monocristal 90 (0.22 mol%) g = 2.0043'+OU-'0.0002, 'B. SUP. 0 INF. 2' = 5.35'+OU-'0.25x10-2 cm-1, 'B. SUP. 0 INF. 4'= - 4.03'+OU-'1.4x10-5cm-1, monocristal 99 (0.02 mol%) g = 2.0026'+OU-'0.0004, 'B. SUP. 0 INF. 2' = 5.4'+OU-'0.3x10-2 cm-1, 'B. SUP. 0 INF. 4' = - 8.33'+OU-'1.6x10-5cm-1. Foi medida e analisada a dependência angular da largura das linhas nas duas bandas de freqüências. Através de modelos teóricos (Watanabe, Orbach-Das-Sharma, Spinspin, Spin-spin Spin-órbita) calculamos o parâmetro de desdobramento a campo zero, 'B. SUP. 0 INF. 2', do estado fundamental do íon Fe3+, para determinar qual o sítio que este íon ocupa no LiNbO3.
Título em inglês
ERP of Fe3+ ion in single crystals and fibres of LiNbO3
Palavras-chave em inglês
Crystalline field
ERP
Magnetic impurities
Resumo em inglês
We report EPR measurements of Fe3+ ion in bulk LiNbO3 single crystals and in the form of fibers. Spin Hamiltonian for the Fe3+ ion in a trigonal symmetry (C3v) site is given by: H = 'beta' 'VET.H' 'VET.g' 'VET.S' + 'B20O20+B40O40. Measurements were performed at room temperature and two frequency bands, 10 and 34GHz, using three samples of LiNbO3 with different concentrations of Fe3+ g-factor and the crystal field parameters were found to be: for fiber (0.3 mol% of Fe3+) g = 1.9908 '+OU-' 0.0002, 'B. SUP. 0 INF. 2' = 5.4'+OU-'0.2x10-2 cm-1 , 'B. SUP. 0 INF. 4' = -7.7'+OU-'1.5x10-5cm-1, for the single crystal 90 (0.22 mol%) g = 2.0043'+OU-'0.0002, 'B. SUP. 0 INF. 2' = 5.35'+OU '0.25x10-2 cm-1, 'B. SUP. 0 INF. 4'= - 4.03'+OU-'1.4x10-5 cm-1, and for the single crystal 99 (0.02 mol%) g = 2.0026'+OU-'0.0004, 'B. SUP. 0 INF. 2' = 5.4'+OU-'0.3x10-2 cm-1, 'B. SUP. 0 INF. 4' = - 8.33'+OU-'1.6x10-5cm-1. The angular dependence of the line width were also measured and compared with theoretical model. To determine the substitutional site of Fe3+ ion in the LiNbO3 lattice, we calculated the zero field splitting parameter 'B. SUP. 0 INF. 2' of the ground state, using many theoretical models (Watanabe, Orbach-Das-Sharma, Spin-spin, Spin-Spin Spinorbita).
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Ricardo_Santana_M.pdf (3.23 Mbytes)
Data de Publicação
2008-04-10
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.