Dissertação de Mestrado
DOI
10.11606/D.76.2006.tde-06052008-144955
Documento
Autor
Nome completo
Waldir Avansi Junior
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2006
Orientador
Banca examinadora
Mastelaro, Valmor Roberto (Presidente)
Origo, Fábio Dondeo
Peitl Filho, Oscar
Título em português
Modificação e cristalização do sistema vítreo BaO-B2O3-RO2 (R=Ti, Si) utilizando a radiação de um laser de CO2
Palavras-chave em português
Cristalização
Laser
Vidros boratos
Resumo em português
Este trabalho apresenta um estudo sobre a modificação e cristalização superficial dos sistemas vítreos 40BaO-45B2O3-15TiO2 (BBT) e 42BaO-42B2O3-16SiO2 (BBS) utilizando a radiação proveniente de um laser modulado de CO2. Três diferentes parâmetros experimentais foram avaliados: a potência do laser, o tempo de exposição à radiação e a presença de micropartículas da fase ?-BaB2O4 (?-BBO) na superfície da amostra. As modificações causadas pela exposição das amostras à radiação laser foram caracterizadas através das técnicas de perfilometria, microscopia óptica, espectroscopia micro-Raman e difração de raios X. De uma maneira geral, os resultados mostram que a escolha adequada da potência do laser e do tempo de exposição à radiação leva a uma modificação superficial ou a uma modificação seguida da cristalização superficial da região exposta a radiação. A presença de micropartículas da fase ?-BBO na superfície da amostras influi de maneira significativa no processo de modificação e cristalização superficial. A presença dessas micropartículas induziu a cristalização da fase ?-BBO com um relativo alto grau de orientação preferencial na direção (006), permitindo a observação visual do efeito de geração de segundo harmônico em algumas amostras. Estudos de micro-fotoluminescência mostraram que o íon Sm3+ quando adicionado a matriz vítrea BBT apresenta um alto grau de desordem mesmo em amostras cristalizadas. No entanto, para a matriz BBS, este estudo mostra uma possível incorporação do íon terra-rara na região cristalizada.
Título em inglês
Modification and crystallization of BaOB2O3RO2(R=Ti, Si) glassy system using a CO2 laser radiation source
Palavras-chave em inglês
Borate glasses
Crystallization
Lazer
Resumo em inglês
This work describes a study regarding the permanent modification and/or crystallization of 40BaO-45B2O3-15TiO2 (BBT) and 40BaO-45B2O3-16SiO2 (BBS) glass compositions when exposed to a continuous CO2 laser beam radiation. The effect of three experimental parameters was evaluated: the laser power, the radiation time exposure and the presence of micro-particles of the ?-BaB2O4 crystalline phase on the glass sample surface prior to radiation. The geometry of permanent modification and the crystallization process were characterized by using the perfilometry, optical microscopy, Micro-Raman spectroscopy and X-ray diffraction (XRD) techniques. The results show that the surface modification and crystallization can be controlled by a suitable choice of the laser power and radiation time exposure. In all samples, it was observed that the presence of ?-BaB2O4 micro-particles on the sample surface affects significantly equally the permanent modification and the crystallization process. The preferential orientation of the ?-BaB2O4 on the (006) plane direction allowed the observation of a relative high intense second harmonic generation effect. The micro-photoluminescence study shows that the Sm3+ ion in BBT glass sample present a high degree of disorder, even in the crystallized samples. On the other hand, when added to the BBS glass sample, it seems that the Sm3+ ions are incorporated onto the crystallized region.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2008-05-07
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • AVANSI JUNIOR, W., MASTELARO, VALMOR R, and ANDREETA, Marcelo R. B. Crystallization and densification of the BaO-B2O3-SiO2 glassy system by using a CO2 laser irradiation. In XI International conference on the physics of non crystalline solids, Grecia, 2006. Proceedings of the XI International conference on the physics of non crystalline solids., 2006. Abstract.
  • AVANSI JUNIOR, W., MASTELARO, VR, and ANDREETA, Marcelo R. B. Crystallization and densification of the BaO-B2O3-SiO2 glassy system by using a CO2 laser irradiation. In XI International conference on the physics of non crystalline solids, Rhodes -Grecia, 2006. Proceedings of the XI International conference on the physics of non crystalline solids., 2006. Abstract.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.