• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.75.2014.tde-27012015-090303
Documento
Autor
Nombre completo
Pedro Farinazzo Bergamo Dias Martins
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2014
Director
Tribunal
Ticianelli, Edson Antonio (Presidente)
Calegaro, Marcelo Luiz
Camargo, Pedro Henrique Cury
Título en portugués
Atividade eletrocatalítica e estabilidade de nanopartículas de platina suportadas em óxido de molibdênio e carbono frente à reação de redução de oxigênio
Palabras clave en portugués
catalisadores de platina
célula a combustível de eletrólito polimérico
reação de redução de oxigênio
Resumen en portugués
O envelhecimento dos eletrocatalisadores utilizados em cátodos de células a combustível de eletrólito polimérico (PEMFCs) é um dos principais fatores que restringem sua aplicação como conversores de energia em larga escala. Esse trabalho visa contribuir para o aprimoramento da estabilidade de nanopartículas de platina (NPs de Pt) por meio da modificação do suporte catalítico aos quais encontram-se impregnadas. Desse modo, foram realizadas sínteses de suportes catalíticos baseados em óxidos de molibdênio (MoO3 e MoO2) ancorados em carbono Vulcan® XC72-R, sendo os materiais produzidos caracterizados física, estrutural e eletroquimicamente antes e após a impregnação de NPs de Pt. Para investigar a estabilidade dos eletrocatalisadores, foi realizado um teste de degradação eletroquímico acelerado, o qual consistiu em aplicar os ciclos de potenciais entre 0,6 e 1,0 V vs. ERH por curto período de tempo. Os resultados mostraram que os métodos de síntese utilizados foram satisfatórios, levando a formação dos catalisadores com as proporções bem próximas das requeridas. O catalisador Pt/MoO3-C apresentou a maior atividade específica frente a reação de redução de oxigênio (RRO), atribuída a efeitos sinérgicos metal/suporte. Quando investigada a estabilidade dos materiais frente ao teste de degradação eletroquímico acelerado, observou-se que, a princípio, nenhum dos óxidos de molibdênio diminui a extensão da degradação da platina. Analisando-se as atividades específicas frente à RRO para cada catalisador antes e após o envelhecimento eletroquímico, foi observado que Pt/MoO2-C apresentou-se como o material mais estável dentre os demais.
Título en inglés
Electrocatalytic activity and stability of platinum nanoparticles supported on molybdenum oxides and carbon towards oxygen reduction reaction
Palabras clave en inglés
oxygen reduction reaction
platinum based catalysts
polymer electrolyte membrane fuel cell
Resumen en inglés
The aging of Pt based electrocatalysts used in the polymer electrolyte fuel cell (PEMFC) cathodes is one of the main issues that restrict its wide application as energy converters. This work aims to contribute to the improvement of the stability of platinum nanoparticles (Pt NPs) by modification of the catalyst support at which they are impregnated. Thus, syntheses of catalyst supports based on molybdenum oxide (MoO3 and MoO2) anchored on Vulcan® XC72-R carbon were carried out and the produced materials were characterized physically, structurally and electrochemically prior and after impregnation of the Pt NPs. To investigate their stability, an electrochemical accelerated degradation test was performed, which consisted of applying a large number of short duration potential cycling steps between 0.6 and 1.0 V vs. RHE. The results showed that the synthetic methods used here were satisfactory, leading to the formation of catalysts with compositions near to those expected. The Pt/MoO3-C catalyst showed the highest specific activity toward the oxygen reduction reaction (ORR), and this was attributed to metal/support synergistic effects. When the stability against electrochemical accelerated degradation test of the materials was investigated, it was observed that, in principle, none of the molybdenum oxides really decreases the extent of platinum degradation. However, comparing the specific activities towards the ORR for each catalyst, before and after electrochemical aging, it is concluded that Pt/MoO2-C is the most stable material among all others.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-01-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.