• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Doctoral Thesis
DOI
https://doi.org/10.11606/T.75.2016.tde-25022015-082454
Document
Author
Full name
Fernando de Oliveira
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2014
Supervisor
Title in Portuguese
Lignopoliuretanos: preparação, caracterização e aplicação em compósitos de sisal
Keywords in Portuguese
compósitos
fibras de sisal
lignopoliuretanos
matéria prima de origem renovável
poliuretanas baseadas em lignossulfonato
propriedades mecânicas
Abstract in Portuguese

A valorização racional da lignina e seus derivados é um dos maiores desafios ligado às biorrefinarias em que estas macromoléculas são geradas como subprodutos. Os lignossulfonatos, obtidos através do processo de polpação sulfito da madeira, são produzidos em larga escala e pouco utilizados como reagentes na preparação de compostos macromoleculares. A presença de grupos OH em sua estrutura permite o seu uso como macromonômero na obtenção de poliuretanos (PUs). O presente estudo teve como meta a obtenção de lignopoliuretanos e de compósitos baseados principalmente em matérias primas obtidas a partir de fontes renováveis. O óleo de mamona (OM) e lignossulfonato de sódio (NaLS), ambos oriundos de matérias primas renováveis, foram utilizados, em composições variadas, como substitutos de polióis convencionais, juntamente com difenilmetano diisocianato (MDI), na reação de obtenção de PUs. Inicialmente, PUs foram preparados a partir de NaLS e outros polióis, como dietilenoglicol (DEG), polietilenoglicol (PEG) e OM, assim como a partir destes reagentes, exceto NaLS (amostras controles). Visando aumentar a reatividade das hidroxilas do NaLS frente aos grupos isocianatos na síntese dos lignopoliuretanos, o NaLS foi oxipropilado (reação com óxido de propileno, gerando LS-Oxi) e hidroxialquilado (reações com glutaraldeído e formaldeído, gerando NaLS-Glu e NaLS-For, respectivamente). O uso de aldeídos na modificação do NaLS, até onde se tenha conhecimento, foi uma abordagem inédita no que se refere à síntese de lignopoliuretanos. Os produtos, (LS-Oxi, NaLS-Glu, NaLS-Glu) foram caracterizados por espectroscopia na região do infravermelho (IV) e, associados ou não com OM, foram usados na preparação de lignopoliuretanos (também caracterizados por IV). Fibras lignocelulósicas extraídas de sisal (Agave sisalana), cujo maior produtor mundial é o Brasil, foram utilizadas como reforço dos lignopoliuretanos preparados. Os compósitos lignopoliuretânicos, bem como os lignopoliuretanos não reforçados, foram caracterizados por análise termogravimétrica (TG), resistência ao impacto, resistência à flexão, microscopia eletrônica de varredura (MEV) e análise térmica dinâmico-mecânica (DMA). Os resultados mostraram que as fibras de sisal aumentaram consideravelmente a resistência ao impacto de todos os lignopoliuretanos. Entre os compósitos baseados em NaLS não modificado (Grupo 1), o DEG/NaLS/MDI/Sisal foi o que apresentou melhor resistência ao impacto (472 J m-1) e melhor resistência à flexão (47 MPa). Quando o NaLS oxipropilado foi utilizado (Grupo 2), o compósito LS-Oxi/MDI/Sisal apresentou resistência ao impacto de 459 J m-1 e resistência à flexão de 43 MPa, enquanto que o compósito NaLS-Glu/MDI/Sisal, preparado à partir do NaLS hidroxialquilado (Grupo 3), apresentou resistência ao impacto de 945 J m-1 e resistência à flexão de 23 MPa. As imagens de MEV da superfície de fratura pós-ensaio de impacto revelaram uma forte adesão na interface fibra/matriz, como consequência da presença de ligações hidrogênio entre os grupos uretanos da matriz e os grupos hidroxila das fibras, além das interações entre os domínios hidrofóbicos de ambos, fibra e matriz. Materiais com grau de entrecruzamento diversificados, com características entre elastomérica a termorrígidos, foram obtidos a partir do uso do NaLS e do OM, o que faz com que eles se tornem atrativos para diferentes aplicações, como em partes automotivas e painéis de uso arquitetônico. Neste sentido, e atendendo às expectativas atuais, materiais com excelentes propriedades e com elevada proporção de matérias-primas obtidas de fontes renováveis foram desenvolvidos.

Title in English
Lignopolyurethanes: preparation, characterization and application in sisal composites
Keywords in English
composites
lignopolyurethanes
lignosulfonate-based polyurethanes
mechanical properties
raw material from renewable source
sisal fibers
Abstract in English

The rational valuing of lignin and its derivatives is one of the major challenges in the biorefinery context where these macromolecules are generated as byproducts. Lignosulfonates obtained through the wood sulfite pulping process are produced on a large scale. However, they are rarely used as reagents in the preparation of macromolecular compounds. The presence of OH groups in their structure allows their use as a macromonomer to obtain polyurethanes (PU). This study aimed at obtaining lignopolyurethanes and composites based mainly on raw materials obtained from renewable sources. Castor oil (CO) and sodium lignosulfonate (NaLS), both derived from renewable raw materials, were used in different compositions as replacements for conventional polyols along with diphenylmethane diisocyanate (MDI) in the PU synthesis. Initially, polyurethanes were prepared from NaLS and other polyols such as diethylene glycol (DEG), polyethylene glycol (PEG), and OM, as well as by using these reagents, except for NaLS (control samples). In order to increase the reactivity of the OH groups of NaLS against isocyanates in the lignopolyurethanes synthesis, NaLS was oxypropylated (reaction with propylene oxide, generating LS-Oxy) and hydroxyalkylated (reaction with formaldehyde and glutaraldehyde, generating NaLS-Glu-For NaLS, respectively). The use of aldehydes in the NaLS modification, as far as we know, is a novel approach with regard to the lignopolyurethane synthesis. The products (LS-Oxy, NaLS-Glu, and NaLS-For) were characterized by infrared spectroscopy (IR) and associated or not with CO were also used in lignopolyurethanes preparation (also characterized by IR). Lignocellulosic fibers extracted from sisal (Agave sisalana), which has Brazil as its largest producer in the world, were used as reinforcement for the prepared lignopolyurethanes. Lignopolyurethanic composites and the non-reinforced lignopolyurethanes were characterized by thermogravimetric analysis (TG), impact test, flexural strength, scanning electron microscopy (SEM) and dynamic mechanical analysis (DMA). Results showed that sisal fibers substantially increased the impact strength of all lignopolyurethanes. Among the composites based on unmodified NaLS (Group 1), DEG/NaLS/MDI/Sisal showed the best impact strength (472 J m-1) and the best flexural strength (47 MPa). When the oxypropylated NaLS was used (Group 2), the composite
LS-Oxy/MDI/Sisal showed impact strength of 459 J m-1 and flexural strength of 43 MPa, while the composite NaLS-Glu/MDI/Sisal prepared from the hydroxyalkylated NaLS (Group 3) showed impact strength of 945 J m-1 and flexural strength of 23 MPa. The SEM images of the fracture surface after the impact test revealed a strong adhesion in the fiber/matrix interface as a consequence of the presence of hydrogen bonds between the urethane groups of the matrix and the hydroxyl groups of the fibers, in addition to the interactions between the hydrophobic domains of both fiber and matrix. Materials with different degrees of crosslinking and characteristics from elastomeric to thermoset were obtained from the use of NaLS and CO, which makes them attractive for different applications such as automotive parts and panels for architectural use. In general, materials with excellent properties and prepared with a high proportion of renewable raw materials were developed, thus meeting the current expectations concerning biobased materials.

 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-09-27
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.