Tesis Doctoral
DOI
https://doi.org/10.11606/T.75.2017.tde-04082017-153036
Documento
Autor
Nombre completo
Daniely Ferreira de Queiroz
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Varanda, Laudemir Carlos (Presidente)
Pulcinelli, Sandra Helena
Corbi, Pedro Paulo
Ferreira, Paula Sílvia Haddad
Mazali, Italo Odone
Título en portugués
Nanopartículas magnéticas de ferritas recobertas com sílica e funcionalizadas com vinil silano
Palabras clave en portugués
ferrita
nanopartícula magnética
recobrimento,funcionalização
vinil silano
Resumen en portugués
Com o desenvolvimento da nanociência e da nanotecnologia, as nanopartículas magnéticas vêm sendo cada vez mais gerado interesse devido as inúmeras possíveis aplicações na área de catálise, diagnóstico, pigmentos, sensores, etc. Atualmente, as nanopartículas com potencialidade de aplicação em biomedicina que pode se destacar os as ferritas magnéticas os quais apresentam comportamento superparamagnético a temperatura ambiente. Além dos ligantes funcionais, as nanopartículas magnéticas são geralmente recobertas com polímeros orgânicos ou inorgânicos, destacando-se a sílica, nessa última classe. O sistemas as nanopartículas magnéticas recobertas com sílica formando um sistema casca-caroço, possibilita que o núcleo magnético se mantenha protegido por uma camada polimérica que pode conter grupos funcionais ativos, formando hidridos orgânicos-inorgânicos que devido a sua propriedade hidrofóbica ou hidrofílica dependendo da natureza do ligante de modificação de superfície. Este trabalho foi desenvolvido com intuito de obter nanopartículas magnéticas de ferrita MFe2O4, com (M= Fe, Co, Ni e Cu) com controle de tamanho, forma, composição química e estrutural, dos quais foram sintetizados pelo método de decomposição térmica utilizando diferente precursores metálicos para adequação das melhores condições de síntese. As ferritas magnéticas foram recobrimento com sílica, modificando da superfície da partícula e possibilitando caráter hidrofílico ao sistema casca-caroço, apresentando uma melhor estabilidade coloidal em dispersão aquosa devido a presença de grupos silanois na superfície, bem como uma recobrimento uniforma com apenas um núcleo magnético sem formação de aglomerados. A funcionalização com o grupo o trietoxivinilsilano, através de reações de condensação via catálise básica ou ácida, formou uma rede polimérica Si-O-Si, sendo que a presença do grupo vinil (-CH=CH2) livre na a superfície do sistema casca-caroço foi evidenciado através da técnica de FTIR. Portanto foi possível a obtenção de um sistema hibrido orgânico-inorgânico com a superfície contendo grupo que podem ser reativos, abrindo a possibilidade da utilização deste material para futuros testes de aplicações como sensor multifuncional.
Título en inglés
Magnetic nanoparticles of ferrites coated with silica and functionalized with vinyl silane
Palabras clave en inglés
coating
ferrite
functionalization
magnetic nanoparticle
vinyl silane
Resumen en inglés
In recent decades the development of nanoscience and nanotechnology, magnetic nanoparticles have been increasingly generated interest due to the numerous possible applications in the field of catalysis, diagnosis, pigments, sensors, etc. Currently, the nanoparticles with potential of application in biomedicine that can stand out the magnetic ferrites which have superparamagnetic behavior at room temperature. In addition to the functional binders, magnetic nanoparticles are generally coated with organic or inorganic polymers, especially silica in the latter class. The magnetic nanoparticle systems covered with silica forming a shell-core system allow the magnetic core to remain protected by a polymeric layer that may contain active functional groups, forming organic-inorganic hydrides that due to its hydrophobic or hydrophilic property depending on the nature of the surface modifying binder. This work was developed to obtain magnetic nanoparticles of MFe2O4 ferrite, with (M = Fe, Co, Ni and Cu) control of size, shape, chemical and structural composition, of which were synthesized by the thermal decomposition method using different precursors to suit the best conditions of synthesis. The magnetic ferrites were coated with silica, modifying the surface of the particle and allowing a hydrophilic character to the shell-core system, presenting a better colloidal stability in aqueous dispersion due to the presence of silane groups on the surface, as well as a uniform coating with only one magnetic core without formation of agglomerates. The functionalization with the triethoxyvinylsilane group, through condensation reactions via basic or acid catalysis, formed a Si-O-Si polymer network, and the presence of the free vinyl group (-CH=CH2) on the shell surface was observed by FTIR technique. Therefore, it was possible to obtain an organic-inorganic hybrid system with the surface containing the reactive group, opening the possibility of using this material for tests of future applications as multifunctional sensor.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-08-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.