Dissertação de Mestrado
DOI
10.11606/D.75.2010.tde-23062010-164224
Documento
Autor
Nome completo
Monise Cristina Ribeiro Casanova
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2010
Orientador
Banca examinadora
Machado, Sergio Antonio Spinola (Presidente)
Crespilho, Frank Nelson
Varanda, Laudemir Carlos
Título em português
Síntese, caracterização e estudo da estabilidade de nanopartículas metálicas estabilizadas com polieletrólitos e tióis
Palavras-chave em português
Estabilidade
Nanopartículas
Tiol
Resumo em português
Nanomateriais, incluindo as nanopartículas e nanotubos, tem sido extensivamente utilizados em diversas aplicações tecnológicas, devido principalmente às suas interessantes propriedades, advindas da alta relação área/volume. Para a efetiva aplicação destes materiais em dispositivos nanotecnológicos, no entanto, é crucial o desenvolvimento de sistemas altamente estáveis, que mantenham suas propriedades por longos períodos. Neste trabalho foi proposta uma rota sintética para a preparação de nanopartículas de ouro na presença de polieletrólitos e tióis numa só fase, juntamente com um estudo sistemático da estabilidade dos sistemas produzidos. Os espectros de UV-vis obtidos demonstraram a formação de nanopartículas de ouro, com banda plasmônica característica. As nanopartículas foram também visualizadas por imagens de microscopia de Transmissão. Análise de espectroscopia na região do infravermelho (FTIR) mostraram as ligações químicas que ocorrem entre os materiais constituintes dos sistemas híbridos de AuNPs. O estudo de estabilidade das AuNps foi realizado com medidas de espalhamento de luz dinâmico (DLS) bem como por medidas de UV-vis, o que permitiu a obtenção do tipo de solução e condições mais estáveis. Através de análise estatística, por meio da análise de componentes principais (PCA), foi possível verificar quais fatores influenciam de forma significativa a estabilidade das diferentes soluções preparadas.
Título em inglês
Synthesis, characterization and stabilization study of metallic nanoparticles stabilized by thiol and polyelectrolytes
Palavras-chave em inglês
Nanoparticles
Stabilization
Thiol
Resumo em inglês
The use of nanomaterials - including nanoparticles and nanotubes - for technological applications has received tremendous attention in the last few years, mainly due to their unique, size-dependent properties. The proper application of such nanomaterials in technological devices, however, has been limited by parameters such as their physical or chemical stability. In this Master´s dissertation, we introduce a single step synthetic route for preparation of gold nanoparticles in the presence of polyelectrolytes and thiols, with emphasis on the stability of the nanomaterials under different storage conditions. Four different hybrid nanoparticles had been investigated, containing either PAH or PVA as the polymeric phase, in the presence of 3-AMP or 11-AMP thiols, respectively. After synthesis, the formation of the Au nanoparticles (AuNPs) was evidenced by UV-vis spectroscopy, upon appearance of a characteristic plasmonic band centered at ca. 510 or 540 nm, depending on the stabilizing agents used. The AuNPs were also investigated via TEM images. FTIR analyses evidenced that electrostatic interactions occurred between the thiols and the polyelectrolytes, within the hybrid nanoparticles structure. The stability of the four different systems was detailed investigated using UV-Vis spectroscopy, dynamic light scattering (DLS), and visual analyses. The data pointed to the higher stability presented by the AuNps stabilized with PAH in the presence of 3-AMP (PAH/3-AMP AuNPs). In contrast, the AuNPs stabilized with PVA exhibited the lowest stability. This feature was corroborated by statistical analysis, using principal component analysis (PCA), through which was possible to identify the main factor affecting AuNPs stability.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2010-09-09
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.