Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.75.2006.tde-16042007-111408
Document
Auteur
Nom complet
Eurico Yuji Tanabe
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2006
Directeur
Jury
Assaf, Elisabete Moreira (Président)
Giudici, Reinaldo
Vielstich, Teresa Benita Iwasita de
Titre en portugais
"Óxidos do tipo Perovskitas para reações de decomposição direta de NO e redução de NO com CO"
Mots-clés en portugais
decomposição
NO
Perovskita
Resumé en portugais
Uma tecnologia importante para reduzir a quantidade de poluentes atmosféricos lançados na atmosfera, é a utilização de catalisadores, que convertem os gases altamente poluentes como o NO, para outros gases inofensivos ao meio ambiente. Neste trabalho, os óxidos do tipo perovskitas La2CuO4, LaNiO3, LaMnO3, La1,4Sr0,6CuO4, La0,7Sr0,3NiO3 e La0,7Sr0,3MnO3 foram preparados através do método da co-precipitação, caracterizados por difração de raios-X, redução a temperatura programada, fisissorção de nitrogênio e análise química, e, posteriormente avaliados frente as reações de redução de NO com CO, e decomposição direta de NO. Ambas as reações foram testadas nas temperaturas de 400oC e 500oC e o tempo de reação foi de 7 à 10 horas. Através dos ensaios catalíticos verificou-se que o catalisador La2CuO4 apresentou a maior atividade para a reação de redução, e quando substituiu-se parcialmente o lantânio pelo estrôncio, houve uma melhora significativa para todos os catalisadores. As análises de DRX indicaram que, mesmo após os ensaios catalíticos, a estrutura cristalina dos catalisadores foi preservada.
Titre en anglais
"Reduction of NO by CO and direct decomposition of NO on perovskite-type oxide"
Mots-clés en anglais
decomposition
NO
Perovskite
Resumé en anglais
A important technology to reduce the atmospheric pollution is the use of catalysts, to transform high pollutant as NO in other inoffensive gases to the environment. In this work, the perovskite oxides La2CuO4, LaNiO3, LaMnO3, La1,4Sr0,6CuO4, La0,7Sr0,3NiO3 e La0,7Sr0,3MnO3 were prepared through co-precipitation method and characterized by X-ray diffraction and temperature programmed reduction, nitrogen physsisorption and subsequent valued on the reduction of NO by CO and the direct decomposition of NO. These reaction were tested at 400oC and 500oC temperatures and times of reaction between 7 and 10 hours. Through the catalytic tests the La2CuO4 catalyst shown the best activity to the reduce reaction, and when the La is partially substituted by strontium all the catalyst showed a better significant for all the catalysts. The XRD analysis shown that the catalytic structure of the catalysts were preserved after the catalytic test yet.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EuricoYujiTanabe.pdf (1.11 Mbytes)
Date de Publication
2007-04-16
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.