Dissertação de Mestrado
DOI
10.11606/D.54.1978.tde-16032015-105640
Documento
Autor
Nome completo
Edgar Dutra Zanotto
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1978
Orientador
Banca examinadora
Mascarenhas, Yvonne Primerano
Qualifik, Paul
Título em português
Separação de fases amorfas e nucleação de cristais em vidros do sistema Li2O-Si02
Palavras-chave em português
Não disponível
Resumo em português
Foram estudados vidros do sistema Li2O - SiO2, com 29,0 31,0 e 33,3% mol de Li2O, em regiões adjacentes à fronteira de imiscibilidade metaestável. Amostras foram obtidas por meio da técnica de splat cooling. Caracterizou-se o desenvolvimento da separação de fases amorfas com o tratamento térmico, através da evolução da intensidade integrada do espalhamento de raios-X a baixos ângulos. Utilizando-se de microscopia ótica de reflexão e métodos estereológicos, definiu-se a cinética de nucleação de cristais, mostrando-se de maneira clara que a separação de fases acelera a nucleação cristalina em vidros desse sistema. Observou-se também, que esse efeito é mais acentuado durante o estágio de nucleação e crescimento da separação amorfa que na etapa de coarsening. Os resultados obtidos experimentalmente, sugerem que o gradiente de concentração existente na vizinhança das partículas vítreas separadas, contribui apreciavelmente à aceleração da nucleação de cristais. Um aumento significativo da mobilidade atômica, através das interfaces das fases amorfas, poderia ser uma explicação alternativa ou complementar para o efeito verificado. Adicionalmente, mostrou-se as razões pelas quais vários autores concluíram que a separação amorfa não influencia a nucleação cristalina
Título em inglês
Not available
Palavras-chave em inglês
Not available
Resumo em inglês
Phase separation and its influence on crystal nucleation in Li2O - SiO2 glasses were studied. Samples having 29,0%, 31,0% and 33,3% mol Li2O were obtained by the splat cooling technique. The development of amorphous phase separation with heat treatment was characterized by determining the evolution of the integrated intensity of small angle x-rays scattering. Using the optical reflection microscopy and stereological techniques, the kinetics of crystal nucleation was defined, and it was proved that phase separation accelerates crystal nucleation in glasses belonging to this system. It was also observed that this effect is more pronounced during the nucleation and growth stage of amorphous separation than during the coarsening stage. The experimental results suggest that the depleted zone around the separated vitreous particles plays an important role on the acceleration of crystal nucleation. The increase in atomic mobility through the interfaces of the amorphous phases could be an alternative or complementary explanation to the observed effect. Additionally, arguments were given to explain why several authors found that that amorphous separation does not influence crystal nucleation
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2015-03-16
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.