Doctoral Thesis
DOI
10.11606/T.54.1986.tde-16032015-103214
Document
Author
Full name
Choyu Otani
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 1986
Supervisor
Committee
Aegerter, Michel Andre
Craievich, Aldo Felix
Luengo, Carlos Alberto
Mascarenhas, Yvonne Primerano
Torriani, Iris C Linares de
Title in Portuguese
Variações estruturais e de propriedades físicas do coque de lignina
Keywords in Portuguese
Não disponível
Abstract in Portuguese
A lignina, subproduto da obtenção de álcool a partir da madeira, foi analisada quimicamente, verificando-se que contém aproximadamente 35% em peso de carbono fixo e um baixo teor de cinzas (0,70% em peso). Este material foi tratado termicamente a diferentes temperaturas, entre 300 e 2600°C, sob atmosfera inerte, obtendo-se coques com estrutura, composição química e propriedades físicas variadas. A caracterização estrutural dos coques de lignina tratados a diferentes temperaturas foi efetuada por meio da técnica de difração de raio-X, de espalhamento de raio-X a baixo engulo e de espectrofotometria de absorção ótica na região do infravermelho. A correlação da caracterização estrutural com a composição química e com as características físicas, dos coques obtidos, permitiu formalizar um modelo estrutural da transformação deste material em escalas a nível atômico e "macroscópico". Os resultados obtidos das caracterizações possibilitaram indicar as temperaturas adequadas dos tratamentos térmicos, a serem escolhidas, conforme as exigências da aplicação do coque a ser obtido
Title in English
Not available
Keywords in English
Not available
Abstract in English
The studied lignin is a by-product of the process of ethanol production from eucaliptus. It was heat-treated under inert atmosphere conditions at increasing temperatures from 300°C up to 2600°C. This material has about 35 weight % of carbon yield and low ash content (0.70 w %). The structural variations were studied by wide-angle X-ray diffraction, small-angle X-ray scattering and infra-red spectroscopy. The bulk and the "real" density of the samples have also been determined as a function of the heat treatment temperatures. These experimental results enabled us to establish a mechanism of structure variation based on the formation of a graphite-like and porous structure within the initially amorphous lignin matrix. It has been possible to specify the adequate heat treatment temperature based upon the lignin coke applications
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
ChoyuOtaniD.pdf (13.50 Mbytes)
Publishing Date
2015-03-16
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.