Dissertação de Mestrado
DOI
10.11606/D.54.1989.tde-08042015-211626
Documento
Autor
Nome completo
Helder Nunes da Cunha
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1989
Orientador
Banca examinadora
Alfaro, Renê Armando Moreno
Faria, Roberto Mendonça
Motisuke, Paulo
Título em português
Efeito da radiação ultravioleta na despolarização termoestimulada de filmes de Teflon-Fep
Palavras-chave em português
Não disponível
Resumo em português
Um estudo sistemático de despolarização termoestimulada (DTE) foi feito com filmes de Teflon-Fep irradiados com luz ultravioleta. As amostras foram irradiadas em três diferentes situações, na temperatura ambiente: a) Sem contatos metálicos, b) Com contatos metálicos, mas descarregadas e c) Com contatos metálicos, mas previamente carregadas. Foram utilizados contatos de In, Al, Zn, Cu, Cr e Au. As amostras carregadas negativamente despolarizaram-se quase na sua totalidade quando tinham sido irradiadas e estavam com contatos de In, Al e Zn, além de apresentarem sensíveis alterações nas curvas de DTE quando comparadas com as normais. As amostras com os outros contatos metálicos não foram muito alteradas pela radiação. Usando um modelo simplificado foi possível analisar as respostas do pulso térmico das amostras com carga residual e mostrou-se que houve injeção de buracos no caso das amostras irradiadas e carregadas negativamente. Medidas separadas usando amostras com dois contatos levaram à mesma conclusão. As amostras carregadas positivamente apresentaram uma carga residual considerável nas amostras irradiadas, evidenciando a presença de armadilhas profundas para buracos no volume do Teflon-Fep
Título em inglês
Not available
Palavras-chave em inglês
Not available
Resumo em inglês
A systematic study of corona charged Teflon-Fep films previously irradiated with ultraviolet light by the thermal stimulated depolarization (TSD) was performed. The free surface was UV irradiated at room temperature under three different conditions: a) without a metallic contact on the other surface in a not yet charged sample. b) With a metallic contact in a not yet corona charged and c) With a metallic contact in a charged sample. Metallic contacts of In, Al, Zn, Cu, Cr and Au were used. The negatively charged samples become almost totally depolarized after the TSD when irradiated in both cases (b) and (c) of coated with In, Al and Zn contacts, showing also visible changes in the TSD curves as compared with the normal ones. Samples coating with Cu, Cr and Au contacts did not present major changes by the effect of UV radiation. Also, no effect was observed in case (a) whatsoever the nature of the electrode used. The analysis of the residual charge using the Heat Pulse Method (HPM) showed that positive charge was injected by the back electrode. Measurements with samples prepared as incase (b) above but now with a second contact seem also to indicate injection of positive charge. A simplified model is presented in order to explain the heat pulse response of negative irradiated samples. Positively corona charged samples under (a), (b) and (c) UV irradiation give different thermograms as compared as in unirradiated samples. The interpretation of the results is now more difficult but it seems that new deep hole traps are created by UV light
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2015-04-09
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.