Tesis Doctoral
DOI
https://doi.org/10.11606/T.54.1990.tde-06042009-111746
Documento
Autor
Nombre completo
Silvio Rainho Teixeira
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1990
Director
Tribunal
Mascarenhas, Yvonne Primerano (Presidente)
Francisco, Regina Helena Porto
Oliva, Glaucius
Rodrigues, José de Anchieta
Zanotto, Edgar Dutra
Título en portugués
Caracterização da formação de nitretos na liga NbTi 50% por difração de raios-x.
Palabras clave en portugués
Difração de raios-X
Ligas de nióbio
Ligas de titânio
Nitretação
Nitretos de titânio
Resumen en portugués
A nitretação da liga NbTi 50% em peso de Ti, foi examinada em uma atmosfera de nitrogênio, na faixa de temperatura 800-1000°C, utilizando-se a técnica de difratometria de raios-X, microscopia eletrônica de varredura (MEV) e metalografia. Foi observada a formação de duas camadas contínuas de nitretos sobre a matriz: fase-δ (TiN) mais externa e a fase-ξ(Ti2N) mais interna. As duas camadas cresceram continuamente durante a reação, sendo que, a frente de saturação da matriz, pelo nitrogênio, cresceu mais rapidamente do que a frente de saturação do TiN. Foi proposto um método, utilizando-se dados de difratometria de raios-X, para se estudar o crescimento de camadas, sobre metais e ligas, formadas durante a reação com gases. A aplicação deste método permitiu fazer uma avaliação da cinética de crescimento da camada de TiN sobre a camada de Ti2N. A energia de ativação para o crescimento do TiN foi de 19 Kcal/mol, obtida a partir da lei temporal linear, e indicou um mecanismo não controlado pela difusão do nitrogênio através da camada de TiN. Os resultados obtidos indicam que o nitrogênio difunde através de túneis, ricos em Nb, onde sua difusão é mais rápida do que através do TiN.
Título en inglés
Characterization of nitrides formation on NbTi 50% weight alloy by X-ray diffraction.
Palabras clave en inglés
Niobium alloys
Nitridation
Titanium alloys
Titanium nitrides
X-ray diffraction
Resumen en inglés
The NbTi (50% wt. Ti) alloy nitretation under nitrogen atmosphere (p=760mm) at 800-1000°C was studied by X-ray diffractometry, TEM and optical metallograpy. During the reaction the two phases (Ti2N δ and TiN ξ) growed continuously, the (Ti2N, N2) reaction front growed faster than the (TiN, N2). A method for study the scale growing was proposed using X-ray diffractometry data. By using this method, the growth of TiN scale was analyzed and the activation energy of 19 Kcal/mol was determined using a linear timming Law indicating a mechanism not controlled by diffusion througth TiN layer. The present results suggest that the diffusion through the tight tunnels, rich in Nb, allow a fast transport of nitrogen through the TiN layer.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-04-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.