Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.54.1993.tde-03062014-101215
Document
Auteur
Nom complet
Rosa Maria Fernandes Scalvi
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1993
Directeur
Jury
Grandini, Carlos Roberto (Président)
Eiras, José Antonio
Shukla, Madan Mohan
Titre en portugais
Relaxações anelásticas devido a reorientação induzida por tensão de defeitos pontuais em nióbio e tântalo
Mots-clés en portugais
Anelasticidade
Atrito interno
Defeitos pontuais
Resumé en portugais
Esta dissertação mostra a análise da interação de intersticiais pesados como oxigênio e nitrogênio em amostras policristalinas de nióbio e monocristalinas de nióbio e tânalo. Os dados experimentais foram obtidos através de medidas de atrito interno e freqüência de oscilação do pêndulo em função da temperatura, utilizando-se um pêndulo de torção invertido tipo Kê. Os resultados mostram estruturas de relaxação atribuídas à reorientação induzida por tensão de átomos intersticiais em torno de átomos da matriz metálica. Estas estruturas forma analisadas através de dois métodos: subtrações sucessivas e tempo de relaxação. A partir das medidas de atrito interno foram identificados os processos de relaxações Nb-O, Nb-N e Ta-O. Esses mesmos processos de relaxação foram confirmados por meio das medidas de freqüência de oscilação do pendulo usando um método proposto nesta dissertação, o qual relaciona o quadrado dessa freqüência medida e o inverso da temperatura.
Titre en anglais
Anelastic relaxation due to stress induced orderingof point defects in niobium and tantalum
Mots-clés en anglais
Anelasticity
Internal friction
Point defects
Resumé en anglais
This dissertation shows the analysis of heavy interstitials interaction, such as oxygen and nitrogen, in a policrystalline niobium sample and single crystal samples of niobium and tantalum. The experimental data were obtained by internal friction and oscillation frequency measurements as a function of temperature, using a Kê-type inverted torsion pendulum. The results show relaxation structures attributed to stress induced ordering of interstitial atoms around the mettalic matrix atoms. These structures were analysed by two methods: sucessive subtraction and relaxation time. From internal friction measurements, Nb-O, Nb-N and Ta-O relaxation processes were identified. These same relaxation processes were confirmed by oscillation frequency measurements, using a method proposed here, which relates squared frequency with inverse of temperature.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-06-04
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.