Tesis Doctoral
DOI
https://doi.org/10.11606/T.46.2011.tde-28032012-091521
Documento
Autor
Nombre completo
Dulce Magalhães
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Matos, Jivaldo do Rosario (Presidente)
Assunção, João Vicente de
Cosentino, Ivana Conte
Rothschild, Lilian
Serrano, Silvia Helena Pires
Título en portugués
Síntese, caracterização e aplicação de sílica mesoporosa esférica como adsorvente
Palabras clave en portugués
Compostos orgânicos voláteis
Cromatografia a gás
Pluronic P103 e P85 e P123
Rifampicina
Resumen en portugués
Novos tipos de sílicas mesoporosas esféricas (SMEs) com tamanho de partícula entre 3 e 10 µm foram sintetizadas utilizando os copolímeros tribloco EO17PO60EO17 (P103) ou EO26PO39EO26 (P85) como direcionadores de estrutura. As SMEs foram preparadas via um processo de síntese com duas etapas de tratamento hidrotérmico (TH) em forno convencional, utilizando o ortosilicato de tetraetila como fonte de sílica, os surfatantes P103 ou P85 como moldes em combinação com o co-surfatante brometo de cetiltrimetilamônio (CTAB) e o co-solvente etanol, sob condições ácidas. As SMEs obtidas foram caracterizadas por microscopia eletrônica de varredura (MEV) e medidas de adsorção/dessorção de N2. O volume e o tamanho do poro das SMEs podem ser aumentados com o aumento da temperatura do TH. O volume e o tamanho do poro (0,41 cm3g-1; 2,84 nm) da amostra sintetizada com P103 aumentaram (1,20 cm3g-1; 4,32 nm) quando a temperatura do TH aumentou de 80°C para 120°C na segunda etapa do TH. O aumento do volume e do tamanho de poro também pode ser obtido utilizando um único tratamento hidrotérmico, porém empregando 1,3,5-trimetilbenzeno (TMB) como agente dilatador de poros. O volume e o tamanho do poro (0,34 cm3g-1; 2,02 nm) da amostra sintetizada com P85 sem TMB aumentaram (0,37 cm3g-1; 2,51 nm) na amostra preparada com P85 e TMB. As características texturais e de superfície dos materiais obtidos com P103 e P85 foram comparadas com um material sintetizado em paralelo, nas mesmas condições experimentais, utilizando o copolímero EO20PO70EO20 (P123) como direcionador de estrutura e CTAB como co-surfatante. A SME sintetizada com P103 foi usada como adsorvente de compostos orgânicos voláteis (COVs) oriundos de misturas padrões. Os componentes da mistura padrão foram então removidos do adsorvente (sílica) por dessorção térmica e introduzidos em uma coluna cromatográfica para separação por cromatografia a gás (CG) e identificação por espectrometria de massa (EM). Esta SME foi também testada como adsorvente de uma amostra de ar coletada em uma rua com significativo fluxo de veículos. O ar foi coletado paralelamente na SME e num adsorvente comercial (Tenax TA/Carbotrap). Os compostos n-hexano, benzeno, tolueno e o-xileno, oriundos de emissões veiculares, foram encontrados em ambos adsorventes (sílica e Tenax TA/Carbotrap). O fármaco Rifampicina foi encapsulado numa SME sintetizada com P123/CTAB e na sílica SBA-15 (poros ordenados hexagonalmente). A encapsulação do fármaco (cerca de 30%) em ambas as sílicas foi confirmada pelos resultados de adsorção/dessorção de N2.
Título en inglés
Synthesis, characterization and application of spherical mesoporous silica as adsorbent
Palabras clave en inglés
Gas chromatography
Pluronic P103 and P85 and P123
Rifampicin
Volatile organic compounds
Resumen en inglés
New types of mesoporous silica spheres with particle diameter of 3 - 10 µm were synthesized by using a triblock copolymer EO17PO60EO17 (P103) or EO26PO39EO26 (P85) as templates. The microspheres were prepared via a two-step hydrothermal treatment (HT) in an oven by using tetraethoxysilane as silica source, the surfactants P103 or P85 as templates in combination with a cosurfactant cetyltrimethylammonium bromide (CTAB) and a cosolvent ethanol, under acidic conditions. The obtained silica spheres in both procedures were characterized by scanning electron microscopy (SEM) and N2 sorption technique. The volume and the pore size of the silica spheres can become greater by increasing the temperature of the HT. The volume and the pore size (0.41 cm3g-1; 2.84 nm) of the sample prepared with P103 became greater (1.20 cm3g-1; 4.32 nm) when the temperature of HT increased by 80°C to 120°C in the second step of the HT. The volume and the pore size can also be increased using 1,3,5-trimethylbenzene (TMB) as a swelling agent, instead of raising the temperature of the HT. The volume and the pore size (0.34 cm3g-1; 2.02 nm) of the sample prepared with P85 without TMB became greater (0.37 cm3g-1; 2.51 nm) in the sample prepared with P85 and TMB. The characteristics of textures and surfaces of the materials synthesized by using P103 or P85 were compared with a material prepared with the copolymer EO20PO70EO20 (P123) as template using the same experimental conditions. The silica microspheres synthesized with P103 were used as adsorbents for volatile organic compounds (VOCs) from standard mixtures. The compounds of the standard mixture were then removed from the adsorbent (silica) by thermal desorption and introduced into a chromatographic column for separation by gas chromatography (GC) and identification by mass spectrometry (MS). This material was also used as adsorbent of an air sample collected on a street with a significant flow of motor vehicles. The air was collected on the silica and on a commercial adsorbent (Tenax TA/Carbotrap) one by one. The compounds n-hexane, benzene, toluene and o-xylene, resulted from the emissions from vehicles, were found in both adsorbents (silica and Tenax TA/Carbotrap). The drug Rifampicin was encapsulated in the mesoporous spherical silica, prepared with P123/CTAB and in the silica SBA-15 (hexagonally ordered pores). The encapsulation of the drug (about 30%) in both the silica was confirmed by measurements of adsorption/desorption of N2
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-05-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.