Master's Dissertation
DOI
https://doi.org/10.11606/D.46.2016.tde-14042016-103107
Document
Author
Full name
Victor Ferreira Gomes da Silva
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2015
Supervisor
Committee
Bertotti, Mauro (President)
Agostinho, Silvia Maria Leite
Salles, Maiara Oliveira
Title in Portuguese
Estudo da ação de íons cloreto no processo de corrosão por pite utilizando microscopia eletroquímica de varredura
Keywords in Portuguese
Aço inoxidável 304
Corrosão
Microeletrodo
SECM
Abstract in Portuguese
No presente trabalho foi utilizada a microscopia eletroquímica de varredura (SECM) com o objetivo de adquirir informações sobre o processo de corrosão do aço inoxidável 304 em diferentes condições experimentais. Inicialmente, foram realizados ensaios de corrosão com a técnica de voltametria cíclica e acompanhamento do potencial de circuito aberto ao longo do tempo, obtendo-se informações sobre o potencial de circuito aberto e o potencial de pite. Nestes ensaios foram utilizadas soluções de NaCl 0,1 mol L-1 e 0,5 mol L-1 na ausência e presença de O2. Os experimentos com a microscopia eletroquímica de varredura (SECM) foram realizados nas mesmas condições experimentais, em um primeiro momento polarizando o substrato no potencial de circuito aberto específico obtido em cada solução e, em seguida, polarizando-o em 0,5 V (vs Ag/AgCl(KCl sat.)). Trabalhou-se em regiões nas quais havia indícios da formação de pites metaestáveis, monitorando-se o aparecimento de íons Fe(II). Para a realização destes experimentos, o microeletrodo foi polarizado em 0,6V, potencial onde a oxidação de Fe(II) a Fe(III) ocorre em larga extensão. A formação e o rompimento da camada de proteção foram observados de modo generalizado e local. A formação de pite metaestáveis para a solução de NaCl 0,5 mol L-1 também foi notada, sendo esse fato confirmado pela presença de tais pites numa imagem e subsequente desaparecimento na imagem seguinte.
Title in English
Study of the effect of chloride ions and pH in the pitting process using scanning electrochemical microscopy (SECM)
Keywords in English
Corrosion
Microelectrode
SECM
Stainless steel 304
Abstract in English
Scanning electrochemical microscopy (SECM) was used in order to acquire information on the corrosion process of stainless steel 304 at different experimental conditions. Corrosion tests were initially carried out with cyclic voltammetry technique and by monitoring the open circuit potential over time to obtain information about the corrosion potential and the pitting potential. Experiments were performed in 0.1 mol L-1 and 0.5 mol L-1 NaCl solutions, in the absence and presence of O2. Scanning electrochemical microscopy (SECM) experiments were performed under the same experimental conditions, by polarizing the substrate at specific open circuit potential of each solution and then polarizing it at 0.5V (vs. Ag / AgCl (KCl sat.)). Experiments were carried out at regions where there were indications of the formation of metastable pits, by monitoring the appearance of Fe(II) ions. The microelectrode was polarized at 0.6V, a potential value where the oxidation of Fe (II) to Fe (III) occurs to a large extent. The formation and the disruption of the protective layer were noticed widely and locally. The formation of metastable pits in 0.5 mol L-1 NaCl solutions was also noted by analysing such pits in an image and their further disappearance in the following image.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-10-17
 
WARNING: Learn what derived works are clicking here.