Dissertação de Mestrado
DOI
10.11606/D.46.2006.tde-02022007-134525
Documento
Autor
Nome completo
Jocicler Claudio Vieira
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2006
Orientador
Banca examinadora
Agostinho, Silvia Maria Leite (Presidente)
Angnes, Lúcio
Falleiros, Neusa Alonso
Título em português
Estudo de interfases eletroquímicas envolvendo materiais metálicos de uso odontológico
Palavras-chave em português
Corrosão
Eletroquímica
Materiais dentários
Metais
Resumo em português
Interfases "metal - solução eletrolítica de interesse odontológico" foram estudadas a 36,5 graus Celsius por técnicas eletroquímicas estacionárias. Duas ligas, Au-Pt-Pd e Ni-Cr-Mo-Ti, foram comparadas e, neste caso, empregadas a impedância eletroquímica, a microscopia eletrônica de varredura e a espectroscopia de dispersão de energia. Os estudos também incluíram o Ti-cp e a amálgama Ag-Cu-Sn-Zn. Verificou-se o efeito da adição de NaF, de ácido cítrico (H3Cit) e de albumina de soro bovino (BSA) ao meio de NaCl. A liga Ni-Cr-Mo-Ti, desenvolvida para substituir a liga Au-Pt-Pd, apresenta comportamento bem diverso da segunda, caracterizado por uma superfície irreprodutível, potencial de corrosão 200 mV a 500 mV mais negativo, dependendo do meio, e faixa passiva inexistente ou de pequena amplitude de potencial. O Ti-cp está passivado em todo o intervalo de potencial estudado (2 V/ECS) em meios de NaCl e NaCl+H3Cit; em NaCl+NaF, a faixa passiva é bem mais restrita, e a BSA a eleva de 100 mV. O H3Cit destrói o filme passivo sobre as ligas Ni-Cr-Mo-Ti e amálgama. A BSA exerce efeitos distintos dependendo da natureza do material metálico e do meio, sugerindo ora adsorção física, ora ação complexante. São discutidos diferentes tipos de embutimento para as amostras metálicas, como teflon, resinas epóxi e epóxi-vinil-éster (EVER). O embutimento com EVER é o mais recomendável para materiais de uso odontológico.
Título em inglês
Electrochemistry interphases study involving odontologic metallic materials.
Palavras-chave em inglês
Corrosion
Dental materials
Electrochemistry
Metals
Resumo em inglês
Different metal electrolytic interphases with relevance for dental prosthesis and implants were studied at 36,5 degrees Celsius by stationary electrochemical techniques. Two alloys, Au-Pt-Pd and Ni-Cr-Mo-Ti, were compared and in this case, EIS, SEM and EDS were also employed as techniques. The studies also included Ti-cp and Ag-Cu-Sn-Zn amalgam. It was studied the effect of adding NaF, citric acid (H3Cit) and bovine serum albumin (BSA) to NaCl medium. Ni-Cr-Mo-Ti alloy, developed to substitute Au-Pt-Pd alloy, presents a distinct behaviour from the last mentioned alloy, characterized by an irreproducible surface, corrosion potential situated at 200 mV to 500 mV more negative value, depending of the medium, and narrow or absence of passive range. Ti-cp is passive in all the potential range studied (2 V/SCE) in NaCl and NaCl+H3Cit media; in NaCl+NaF the passive range is narrower and it increases 100 mV in the presence of BSA. H3Cit breaks down the passive film deposited on the Ni-Cr-Mo-Ti and amalgam alloy surfaces. BSA exhibits distinct effects depending upon both the nature of the alloy and the media suggesting either physical adsorption either complex formation. Different kinds of polymers for fitting the metallic samples are discussed, such as teflon, epoxy resin and epoxy vinyl ester resin (EVER). The results suggest that the EVER polymer is the most recommendable for fitting dental materials.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2007-02-12
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.