• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Thèse de Doctorat
DOI
https://doi.org/10.11606/T.43.2011.tde-29092011-170342
Document
Auteur
Nom complet
Jim Heiji Aburaya
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2011
Directeur
Jury
Tabacniks, Manfredo Harri (Président)
Chubaci, Jose Fernando Diniz
Dagli, Maria Lucia Zaidan
Partiti, Carmen Silvia de Moya
Zoppa, André Luis do Valle de
Titre en portugais
Modificação superficial de titânio para promoção de osteointegração
Mots-clés en portugais
Biomaterial
Células em cultura
Íons
Titânio
Resumé en portugais
O titânio é considerado um biomaterial (material biocompatível) pela baixa reatividade e pela grande estabilidade da sua camada de óxido superficial. Pelas suas propriedades mecânicas ele é usualmente utilizado na fabricação de substitutos ósseos e implantes dentários. Visando contribuir para o desenvolvimento de novas superfícies osteointegráveis, neste trabalho foram estudadas duas superfícies de titânio modificadas com implantação iônica de P e BF2 com energia de 30 e 77keV, respectivamente. As superfícies foram submetidas a ensaios in vitro de cultura celular de células osteoblásticas (MG-63) e os resultados foram comparados com duas superfícies comerciais: poliestireno tratado para meio de cultura celular (PC) e titânio comum utilizado em implante dentário (TI). A atividade enzimática da fosfatase alcalina (FA) associadas à formação de biofilme mineralizado pelas células diferenciadas foram avaliadas. Concentrações de cálcio e fósforo no biofilme foram determinadas por espectroscopia de raios-X induzida por prótons, PIXE. Imagens superficiais com microscopia eletrônica de varredura serviram para verificar a homogeneidade e integridade dos biofilmes formados. Medidas de ângulo de contato foram realizadas para determinar o caráter hidrofílico das superfícies e do biofilme formado. As superfícies PC e TI se apresentaram hidrofílicas com formação de biofilme menos homogêneo que as apresentadas pelas superfícies PT e BFT, ambas hidrofóbicas. As concentrações de FA medidas no meio de cultura indicaram consumo maior que a secreção em PC e TI. Em PT e BFT foram observados acúmulos de FA no meio de cultura. Concentrações maiores de cálcio e fósforo foram observadas em PC e TI. Destas observações, as quatro superfícies podem ser consideradas biocompatíveis (não citotóxicas) pela formação de biofilme mineralizado e pelas medidas de atividade enzimática.
Titre en anglais
Titanium modification for the promotion of osteointegration
Mots-clés en anglais
Biomaterial
Cell culture
Ion implantation
Titanium
Resumé en anglais
Titanium is considered a biomaterial (biocompatible material) due to its low reactivity and the great stability of its surface native oxide layer. With excellent mechanical properties, titanium is widely used as bone substitutes and dental implants. Aiming to contribute for the development of new surfaces to promote osteoblastic cell grow, two ion-beam-modified titanium samples were compared with two commercially available surfaces: polystyrene treated for cellular cultures (PC), and regular titanium used in dental implants (TI). The modified titanium samples were ion beam implanted with 30 and 77 keV phosphorous and BF2, respectively. All surfaces were employed for in vitro assays using cultures of osteoblastic cells (MG-63). The Phosphatase Alkaline Enzymatic Activity (ALP) was measured and associated with the mineralized bio-film formed by the differentiated cells. The concentration of calcium and phosphorus in the mineralized bio-film was measured by Proton Induced X-ray Emission, PIXE. Scanning Electron Microscope images were used to access the bio-film homogeneity and integrity. Contact angle measurements were used to characterize the wettability of the surfaces and the resulting bio-film. In spite of being more hydrophilic, the surfaces PC and TI formed of a less homogeneous bio-film than the PT and BFT surfaces, which were less hydrophilic. The ALP in the cell culture medium indicated greater consumption than secretion for PC and TI, while for PT and BFT accumulation of ALP was observed. Concentrations of calcium and phosphorus were greater for PC and TI samples. The four surfaces can be considered biocompatible (not cytotoxic) due to mineral bio-film formation and enzymatic activity measurements.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Aburaya.pdf (6.83 Mbytes)
Date de Publication
2011-11-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.