Dissertação de Mestrado
DOI
https://doi.org/10.11606/D.43.2016.tde-22112016-171708
Documento
Autor
Nome completo
Sidney Leal da Silva
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2004
Orientador
Banca examinadora
Pontuschka, Walter Maigon (Presidente)
Barbosa, Luiz Carlos
Muramatsu, Mikiya
Título em português
CARACTERIZAÇÃO ESPECTROSCÓPICA DE VIDROS ALUMINOSSILICATOS E FLUORFOSFATOS DOPADOS COM TÉRBIO (Tb3+)
Palavras-chave em português
Absorção
Luminescência
Óptica
Térbio
Vidro
Resumo em português
Utilizando amostras de vidro aluminossilicato, 21SiO2·9Al2O3·58Tb2O3·4,0MgO·3,0B2O3·2,0ZnO·1,0Sb2O3 (mol%) e fluorfosfato, 7,49NaPO3·16,45MgF2·16,38CaF2·17,66SrF2·11,63BaF2·30,39AlF3 (mol%) adicionado de 8Tb2O3 e 0,5Ce2O (mol), foram realizadas medidas de absorção óptica, tempo de vida de emissões e luminescência nas faixas do ultravioleta e visível dos íons Tb3+. As eficiências quânticas das emissões para o íon Tb3+, 0,90 (90 %), para o vidro aluminossilicato e 0,69 (69 %), para o vidro fluorfosfato, foram determinadas a partir das razões entre os tempos de vida experimentais, obtidos da experiência de tempo de vida e os tempos de vida teóricos, obtidos das informações de absorção óptica e teoria de Judd- Ofelt. As informações de absorção óptica também possibilitaram identificar as prováveis excitações e emissões observadas nos espectros de luminescência em ambos os vidros estudados. Para determinação dos tempos de vida teóricos, foi necessário calcular as probabilidades de transições radiativas que dependem dos parâmetros de Judd-Ofelt, cujos valores encontrados foram 2 = (2,4 ± 0,2)10-19 cm2, 4 = (3,4 ± 0,3)10-20 cm2 e 6 = (1,5 ± 0,2)10-20 cm2, para o vidro aluminossilicato, e 2 = (7,7 ± 0,6)10-20 cm2, 4 = (0,61 ± 0,05)10-20 cm2 e 6 = (0,69 ± 0,06)10-20 cm2, para o vidro fluorfosfato. Tais valores mostraram-se compatíveis aos da literatura pesquisada, confirmando os valores satisfatórios das eficiências quânticas das emissões dos íons Tb3+.
Título em inglês
Spectroscopic Characterization of Glasses Aluminosilicates and Fluorphosphates Doped with Tb3 +
Palavras-chave em inglês
Absorption
Glasses
luminescence
Optics
Terbium
Resumo em inglês
Samples of glasses 21SiO2·9Al2O3·58Tb2O3·4,0MgO·3,0B2O3·2,0Si2O·2,0ZnO·1,0Sb2O3 (mole %) aluminosilicate and 7,49NaPO3·16,45MgF2·16,38CaF2·17,66SrF2·11,63BaF2·30,39AlF3 (mole %) fluorphosphate added of 8Tb2O3 and 0,5Ce2O (mole) were studied by optical absorption, luminescence and emissions lifetime measurements for the Tb3+ ions. The quantum efficiencies of the Tb3+ emissions, 0,90 (90 %), for the aluminosilicate glass and 0,69 (69 %), for the fluorphosphate glass, were determined using the emissions lifetimes and theoretical lifetimes, obtained from the experimental optical absorption data and Judd-Ofelt theory. The information obtained from the optical absorption spectra allowed the identification of the more likely excitations and emissions observed in the luminescence spectra of the glasses. For the determination of the theoretical lifetimes it was necessary to calculate the radiactive transition probabilities which are dependent of the Judd-Ofelt parameters, whose values were found as 2 = (2,4 ± 0,2)10-19 cm2, 4 = (3,4 ± 0,3)10-20 cm2 and 6 = (1,5 ± 0,2)10-20 cm2, for the aluminosilicate, and 2 = (7,7 ± 0,6)10-20 cm2, 4 = (0,61 ± 0,05)10-20 cm2 and 6 = (0,69 ± 0,06)10-20 cm2, for the fluorphosphate glasses. The results are in good agreement literature examined, and confirm the satisfactory values of the quantum efficiency for the Tb3+ emissions.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2016-12-15
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2024. Todos os direitos reservados.