• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.43.2016.tde-22112016-171708
Documento
Autor
Nombre completo
Sidney Leal da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2004
Director
Tribunal
Pontuschka, Walter Maigon (Presidente)
Barbosa, Luiz Carlos
Muramatsu, Mikiya
Título en portugués
CARACTERIZAÇÃO ESPECTROSCÓPICA DE VIDROS ALUMINOSSILICATOS E FLUORFOSFATOS DOPADOS COM TÉRBIO (Tb3+)
Palabras clave en portugués
Absorção
Luminescência
Óptica
Térbio
Vidro
Resumen en portugués
Utilizando amostras de vidro aluminossilicato, 21SiO2·9Al2O3·58Tb2O3·4,0MgO·3,0B2O3·2,0ZnO·1,0Sb2O3 (mol%) e fluorfosfato, 7,49NaPO3·16,45MgF2·16,38CaF2·17,66SrF2·11,63BaF2·30,39AlF3 (mol%) adicionado de 8Tb2O3 e 0,5Ce2O (mol), foram realizadas medidas de absorção óptica, tempo de vida de emissões e luminescência nas faixas do ultravioleta e visível dos íons Tb3+. As eficiências quânticas das emissões para o íon Tb3+, 0,90 (90 %), para o vidro aluminossilicato e 0,69 (69 %), para o vidro fluorfosfato, foram determinadas a partir das razões entre os tempos de vida experimentais, obtidos da experiência de tempo de vida e os tempos de vida teóricos, obtidos das informações de absorção óptica e teoria de Judd- Ofelt. As informações de absorção óptica também possibilitaram identificar as prováveis excitações e emissões observadas nos espectros de luminescência em ambos os vidros estudados. Para determinação dos tempos de vida teóricos, foi necessário calcular as probabilidades de transições radiativas que dependem dos parâmetros de Judd-Ofelt, cujos valores encontrados foram 2 = (2,4 ± 0,2)10-19 cm2, 4 = (3,4 ± 0,3)10-20 cm2 e 6 = (1,5 ± 0,2)10-20 cm2, para o vidro aluminossilicato, e 2 = (7,7 ± 0,6)10-20 cm2, 4 = (0,61 ± 0,05)10-20 cm2 e 6 = (0,69 ± 0,06)10-20 cm2, para o vidro fluorfosfato. Tais valores mostraram-se compatíveis aos da literatura pesquisada, confirmando os valores satisfatórios das eficiências quânticas das emissões dos íons Tb3+.
Título en inglés
Spectroscopic Characterization of Glasses Aluminosilicates and Fluorphosphates Doped with Tb3 +
Palabras clave en inglés
Absorption
Glasses
luminescence
Optics
Terbium
Resumen en inglés
Samples of glasses 21SiO2·9Al2O3·58Tb2O3·4,0MgO·3,0B2O3·2,0Si2O·2,0ZnO·1,0Sb2O3 (mole %) aluminosilicate and 7,49NaPO3·16,45MgF2·16,38CaF2·17,66SrF2·11,63BaF2·30,39AlF3 (mole %) fluorphosphate added of 8Tb2O3 and 0,5Ce2O (mole) were studied by optical absorption, luminescence and emissions lifetime measurements for the Tb3+ ions. The quantum efficiencies of the Tb3+ emissions, 0,90 (90 %), for the aluminosilicate glass and 0,69 (69 %), for the fluorphosphate glass, were determined using the emissions lifetimes and theoretical lifetimes, obtained from the experimental optical absorption data and Judd-Ofelt theory. The information obtained from the optical absorption spectra allowed the identification of the more likely excitations and emissions observed in the luminescence spectra of the glasses. For the determination of the theoretical lifetimes it was necessary to calculate the radiactive transition probabilities which are dependent of the Judd-Ofelt parameters, whose values were found as 2 = (2,4 ± 0,2)10-19 cm2, 4 = (3,4 ± 0,3)10-20 cm2 and 6 = (1,5 ± 0,2)10-20 cm2, for the aluminosilicate, and 2 = (7,7 ± 0,6)10-20 cm2, 4 = (0,61 ± 0,05)10-20 cm2 and 6 = (0,69 ± 0,06)10-20 cm2, for the fluorphosphate glasses. The results are in good agreement literature examined, and confirm the satisfactory values of the quantum efficiency for the Tb3+ emissions.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-12-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.