Thèse de Doctorat
DOI
10.11606/T.43.2002.tde-13122013-135106
Document
Auteur
Nom complet
João Tertuliano Nepomuceno Agra
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2002
Directeur
Jury
Mendonça Filho, Christovam (Président)
Bonagamba, Tito Jose
Isotani, Sadao
Pontuschka, Walter Maigon
Saxena, Rajendra Narain
Titre en portugais
Relaxação da magnetização nuclear de água confinada em alumina
Mots-clés en portugais
Magnetização nuclear
Meios porosos
Relaxação
Resumé en portugais
Neste trabalho é investigada a relaxação longitudinal da magnetização nuclear de água impregnada em pastilhas de pó de alumina (Al IND. 2 O IND. 3) com grau de pureza de 99,8%, objetivando a determinação do diâmentro de poro de uma espuma cerâmica do mesmo material a partir de medidas do tempo de relaxação longitudinal T IND. 1. O trabalho fundamenta-se no fato dos tempos de relaxação da magnetização nuclear T IND. 1 e T IND. 2, spin-rede e spin-spin respectivamente, de um fluido confinado em um meio poroso serem menores que tempos T IND. 1B e T IND. 2B para o mesmo fluido não confinado. Mediram-se os tempos T IND. 1 para graus de impregnação de água nas amostras entre 10 e 100% usando um espectrômetro montado a partir de módulos comerciais e de um gerador de pulsos desenvolvido no IFSC-USP. A partir dos tempos T IND. 1 e dos diâmetros de poro das pastilhas de pó, determinou-se o valor da relaxatividade longitudinal ou intensidade de relaxação superficial (mu IND. 1), um parâmetro que caracteriza a interface água-alumina nestas amostras. Usando o valor de (mu IND. 1) obtido para o pó e o tempo de relaxação T IND. 1 medido nas amostras de espuma cerâmica foi determinado o diâmetro de poro desta. Última, o qual é comparado com os valores obtidos com a microscopia eletrônica e com a injeção de mercúrio. O caráter não invasivo desta técnica em contraste com as outras, faz dela a única possível em algumas aplicações.
Titre en anglais
Relaxation of the nuclear magnetization water contained in alumina.
Mots-clés en anglais
Nuclear magnetization
Porous media
Relaxation
Resumé en anglais
Nuclear magnetization relaxation of water imbibed on 99,8% purê alumina (Al IND. 2 O IND. 3) grain packs is investigated aiming to determine the mean pore diameter of ceramic foam pieces of the same material. The work rely on the shortening of the relaxation times T IND. 1 spin-lattice and T IND. 2 spin-spin of the nuclear magnetization of fluids confined on porous media as compared with their T IND. 1B e T IND. 2B bulk values. Relaxation times T IND. 1 were measured, using a spectrometer built from commercial modules and a pulse generator developed at the IFSC-USP, varying the content of water imbibed from 10 to 100%. The longitudinal relaxation (mu IND. 1), or surface sink strength, was determined from the measured T IND. 1 values and the mean pore diameter of the powder packs. This parameter characterizes the water-alumina interface of these samples. Using the (mu IND. 1) value from the powder and the relaxation times T IND. 1 measured on the ceramic foam pieces, the mean pore diameter of these samples were determined and are compared with the values obtained from mercury intrusion and electron microscopie. The non-invasive character of this technique distinguishes it from the other, making it the only possible in some applications.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
RE34963Agra.pdf (1.05 Mbytes)
Date de Publication
2014-02-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.